含铬铝泥制备纳米AlO(OH)片 被引量:2

Preparation of nano Al O(OH) flake from chromium-containing alumina sludge
下载PDF
导出
摘要 含铬铝泥是一种危险固体废弃物.以含铬铝泥酸溶液为原料,采用沉淀法制备了纳米AlO(OH)片,并对样品进行了XRD、FT-IR、SEM表征分析.研究结果表明,随着加水量增加,含铬铝泥的溶解率增大,当水的加入量为10 mL/g泥时,含铬铝泥的溶解率最大;随着H2SO4加入量的增加,含铬铝泥的溶解率增大,且当H2SO4加入量为9mL/(g泥)时,含铬铝泥的溶解率最大;随着溶解温度的升高,含铬铝泥的溶解率增大,且当溶解温度为70℃时,含铬铝泥的溶解率最大.采用含铬铝泥制备的样品为厚约8 nm、长宽约为100~200 nm分散性较好的片状纳米AlO(OH). Chromium-containing alumina sludge is a kind of dangerous solid waste. The nano A10(OH) flakes are prepared from its acid solution by precipitation method. The samples are characterized by XRD, FT-IR and SEM. The results show that increasing the amount of water or sulfuric acid or dissolving temperature all leads to the increase of the solubility of chromium-containing alumina sludge. When the amount of water and sulfuric acid is 10 and 9 mL per gram chromium-containing alumina sludge, respectively, or at 70℃ of dissolving temperature, the highest solubility of chromium-containing alumina sludge can be achieved. The sample prepared from chromium-containing alumina sludge is nano A10(OH) flake with about 8 mn in thickness, 100 -200 nm in length and width,which has good dispersibility.
作者 李微 孙彤
出处 《现代化工》 CAS CSCD 北大核心 2015年第2期73-76,共4页 Modern Chemical Industry
基金 中华环境保护基金会格平绿色行动辽宁环境科研教育"123工程"资助项目(CEPF2012-123-2-5) 辽宁省教育厅科学技术研究项目(L2013429)
关键词 含铬铝泥 AlO(OH) 纳米 片状 chromium-containing alumina sludge AlO (OH) nanometer flake
  • 相关文献

参考文献9

二级参考文献115

共引文献66

同被引文献26

  • 1郑敏,李先荣,孟艳艳,廖辉伟.氯化焙烧法回收铬渣中的铬[J].化工环保,2010,30(3):242-245. 被引量:13
  • 2谷军,宋开伟,钱觉时.铬渣特性及解毒利用技术[J].粉煤灰,2007,19(2):32-34. 被引量:8
  • 3付凌雁,张召述,娄东民,李太昌.铝土矿尾矿活化制备水泥基材料的研究[J].化学工程,2007,35(6):41-44. 被引量:15
  • 4Achal Varenyam, Pan Xiangliang, Lee Duu-Jong, et al. Remediation of Cr (VI) from chromium slag by biocemen- tation[J]. Chemosphere, 2013, 93 (7) : 1352 - 1358.
  • 5Mao Linqiang, Gao Bingying, Deng Ning, et al. The role of temperature on Cr (VI) formation and reduction dur- ing heating of chromium-containing sludge in the presence ofCaO[J].Chemosphere, 2015, 138: 197-204.
  • 6Fonseca-Correa R, Giraldo L, Moreno-Pirajan J C. Trivalent chromium removal from aqueous solution with physically and chemically modified corncob waste [ J ]. J AnalApplPyrolysis, 2013, 101: 132-141.
  • 7刘红.絮凝剂在金属铬生产中的应用探究[C]//中国金属学会铁合金分会.第23届全国铁合金学术研讨会论文集:上.宁夏:中国金属学会铁合金分会,2014:98-100.
  • 8Brodie E L, Joyner D C, Faybishenko B, et al. Mi- crobial community response to addition of polylactate compounds to stimulate hexavalent chromium reduc- tion in groundwater[J]. Chemosphere, 2011, 85(4) : 660 - 665.
  • 9Basu A, Johnson T M, Sanford R A. Cr isotope frac- tionation factors for Cr (VI) reduction by a metabolical- ly diverse group of bacteria [J]. Geochim Cosmochim Acta, 2014, 142: 349-361.
  • 10国家环保总局科技标准司.GB/T15555.7-1995固体废物六价铬的测定硫酸亚铁铵滴定法[S].北京:中国环境科学出版社,1995.

引证文献2

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部