光散射PC荧光树脂的制备及光学性能 被引量:6

Preparation and Luminescent Properties of Light Scattering Fluorescent Resin
下载PDF
导出
摘要 以聚碳酸酯(PC)粉体、有机硅光扩散剂和YAG∶Ce荧光粉为原料,通过熔融共混法和高温压模法及减薄抛光工艺制备出不同有机硅光扩散剂质量分数的PC/YAG∶Ce光散射荧光树脂样品,通过SEM、XRD、透射光谱和PL的性能分析,表明:荧光树脂样品在500~800nm光谱范围有较高的透光率,样品的主相都为Y3Al5O12,在342和448nm有两个激发波峰,发射光谱在532nm有一宽峰,属于Ce3+的5d→4f特征跃迁发射,对应的荧光寿命在61.5ns左右。把荧光树脂样品应用到白光LED器件的封装获得的光效为81.12lm/W@100mA,说明PC/YAG∶Ce荧光树脂片适用于作白光LED封装的新型荧光材料。 With the methods of compound-melting and high-temperature molding,PC/YAG∶Ce fluorescent resin pieces were prepared.The transmittance of the prepared PC/YAG∶Ce fluorescent resin in 500~800nm reaches approximately 65%(0.71 mm thick,double sides polished).The fluorescent resin was characterized by XRD,SEM and PL.The X-ray diffraction(XRD)patterns demonstrated that the fluorescent resin was pure Y3Al5O12 phase.The scanning electron microscopy(SEM)images showed that YAG phosphor was distributed evenly in the fluorescent resin.The excitation spectra had a weak peak at 342 nm and a strong band at 448 nm.The broad emission peaks at about 532 nm can be attributed to 5d→4ftransition of Ce3+ions.Decay curves for the fluorescence of PC/YAG∶Ce fluorescent resin show that the lifetime of the fluorescent resin was 61.5ns.The luminous efficacy of the white LED packaged by the fluorescent resin and blue LED chip was 81.12lm·W-1 at 100 mA.All results above of PC/YAG∶Ce fluorescent resin indicate a promising fluorescent material for white LEDs.
出处 《光谱学与光谱分析》 SCIE EI CAS CSCD 北大核心 2014年第12期3178-3182,共5页 Spectroscopy and Spectral Analysis
基金 国家自然科学基金重点项目(61176043) 广东省战略性新兴产业专项资金LED产业项目(2010A081002005 2011A081301003 2012A080304016) 华南师范大学青年教师培养基金(2012kj018) 华南师范大学研究生科研创新基金项目(2012kyjj223)资助
关键词 荧光树脂 YAG∶Ce 聚碳酸酯 白光LED Fluorescent resin YAG∶Ce Polycarbonate White LED
  • 相关文献

参考文献10

二级参考文献110

共引文献161

同被引文献48

  • 1肖瑶,范广涵,皮辉,许毅钦,郑树文,陈志武,贺龙飞,张力,张涛.PC/YAG∶Ce荧光树脂的制备及光谱分析[J].发光学报,2013,34(11):1419-1423. 被引量:4
  • 2肖华,吕毅军,徐云鑫,朱丽虹,陈国龙,高玉琳,范贤光,薛睿超.传统白光LED与远程荧光粉白光LED的发光性能比较[J].发光学报,2014,35(1):66-72. 被引量:32
  • 3曹优明,郑仕远.有机硅改性丙烯酸树脂荧光涂料的研究[J].新型建筑材料,2004,31(10):15-17. 被引量:12
  • 4周建华,游佰强,肖磊,王静,王晨.PMMA改性聚合物薄膜的光学性能研究[J].激光与光电子学进展,2006,43(12):48-52. 被引量:4
  • 5康婧宁.PC表面UV固化有机.无机杂化光扩散涂层材料制备及性能研究[D].上海大学学位论文,2013,5.
  • 6CRAWFORD M H. LEDs for solid-state lighting= per- formance challenges and recent advances[J]. IEEE Jour- nal of Selected Topics in Quantum Electronics, 2009,15 (4): 1028-1040.
  • 7LIU S, LUO X. LED Packaging for Lighting Applica tions[M]. Wiley & Sons,2011.
  • 8HUANG K C, LU W J,LIAO K Y, et al. White LED featuring remote phosphor with poly (vinylidene fluor- ide-co-hexafluoro propylene) [J].Materials Letters, 2014,122(5) :265-268.
  • 9ZHU Y, NARENDRAN N. Investigation of remote phosphor white light-emitting diodes with multi-phos- phor layers[J].Japanese Journal of Applied Physics, 2010,49 (10) : 100203-100203-3.
  • 10YU R,JIN S,CEN S,et al. Effect of the phosphor geom- etry on the luminous flux of phosphor-converted light e- mitting diodes[J].IEEE Photonics Technology Letters, 2010, 22(23):1765- 1767.

引证文献6

二级引证文献12

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部