Characteristics and Mechanism of Modified Triethanolamine as Cement Grinding Aids

Characteristics and Mechanism of Modified Triethanolamine as Cement Grinding Aids
原文传递
导出
摘要 Effects of modified triethanolamine as cement grinding aids on particles characteristics and mechanical property of cement were studied, and its reaction mechanism was analyzed by IR, Zeta potential, SEM, XRD and TG-DTA. The results show that the content of 3-32 μm particles for cement with 0.015% modified triethanolamine(M-TEA) is increased by 12.4%, and the compressive strengths of cement with 0.03% M-TEA are increased by 5.5 and 8.2 MPa at 3 and 28 days, respectively. And both the grinding and enhancement effects of M-TEA on cement are better than triethanolamine. The mechanism analysis shows that M-TEA not only has the amino and hydroxyl groups of TEA, but also has the ester, carbonyl, carboxyl groups which easily combine with metal ions of cement minerals, resulting in that M-TEA can promote surface adsorption and shield the unsaturated charges in the surface and crack section of particles, thus particles reunion is prevented and grinding efficiency is improved. Enhancement of M-TEA on cement mainly lies in that it can promote or induce hydration reaction of cement mineral with gypsum and water, which accelerates formation of hydration products, and then improves the structure and morphology of cement hydration products, thus the uniformity and compactness of product structure is increased. Effects of modified triethanolamine as cement grinding aids on particles characteristics and mechanical property of cement were studied, and its reaction mechanism was analyzed by IR, Zeta potential, SEM, XRD and TG-DTA. The results show that the content of 3-32 μm particles for cement with 0.015% modified triethanolamine(M-TEA) is increased by 12.4%, and the compressive strengths of cement with 0.03% M-TEA are increased by 5.5 and 8.2 MPa at 3 and 28 days, respectively. And both the grinding and enhancement effects of M-TEA on cement are better than triethanolamine. The mechanism analysis shows that M-TEA not only has the amino and hydroxyl groups of TEA, but also has the ester, carbonyl, carboxyl groups which easily combine with metal ions of cement minerals, resulting in that M-TEA can promote surface adsorption and shield the unsaturated charges in the surface and crack section of particles, thus particles reunion is prevented and grinding efficiency is improved. Enhancement of M-TEA on cement mainly lies in that it can promote or induce hydration reaction of cement mineral with gypsum and water, which accelerates formation of hydration products, and then improves the structure and morphology of cement hydration products, thus the uniformity and compactness of product structure is increased.
出处 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2015年第1期134-141,共8页 武汉理工大学学报(材料科学英文版)
基金 Funded by the National Natural Science Foundation of China(No.50872151)
关键词 modified triethanolamine grinding aids CEMENT particles characteristics mechanical property MECHANISM cement hydration modified triethanolamine grinding aids cement particles characteristics mechanical property mechanism cement hydration
  • 相关文献

参考文献5

二级参考文献84

共引文献93

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部