热扩散法电镀黄铜珠光体钢丝湿式拉拔断丝研究 被引量:1

Study on necking fracture of brass-coated steel wire produced by heat diffusion electroplating during wet drawing
下载PDF
导出
摘要 为找出电镀黄铜钢丝湿拉发生颈缩断丝的原因,通过扫描电镜、能谱仪以及X射线衍射仪分析了湿式拉拔正常和异常的钢丝的微观组织和镀层物相,并用拉伸试验机检测了其力学性能。结果发现,2种镀黄铜钢丝的微观组织均为伪共析珠光体,未发现异常的先共析铁素体和球化渗碳体,二者力学性能也无明显差异。湿拉异常的镀黄铜钢丝的镀层中,β-黄铜相的质量分数高达24%,是湿拉正常钢丝的6倍。当镀黄铜钢丝的微观组织和力学性能良好时,镀层中过多的硬脆β-黄铜相是导致湿拉出现颈缩状断口的重要原因。通过在规定温度下对异常钢丝镀层重新做热扩散处理,可使湿拉断丝率从5.0次/t下降至0.1次/t。 To find out the cause of necking fracture during wet drawing of brass-plated steel wires, their microstructures and coating's phases in cases of normal and abnormal wet drawing were studied by scanning electron microscope, energy-dispersive spectrometer, and X-ray diffractometer, and their mechanical properties were tested by tensile testing machine. The results showed that the microstructures of both brass-plated steel wires are pseudo-eutectoid pearlite, no abnormal proeutectoid ferrite or spherical cementite are found, and there is no distinctive difference in mechanical properties between them. The mass fraction of β-brass phase is up to 24% in the coating of the brass-plated steel wire abnormally wet drawn, which is 6 times as large as that in the coating of normally drawn steel wire. The excessive mass fraction of hard and fragile β-brass phase in the coating is the key factor that leads to necking fracture, while the microstructure and mechanical properties of brass-plated steel wire are fine. The wire fracture rate is reduced from 5.0 times per ton to 0.1 time per ton during wet drawing by redoing heat diffusion treatment of the abnormal steel wire at a specified temperature.
作者 钱庆生
出处 《电镀与涂饰》 CAS CSCD 北大核心 2015年第7期404-408,共5页 Electroplating & Finishing
关键词 钢丝 电镀 黄铜 热扩散 湿拉 微观组织 颈缩状断口 steel wire electroplating brass heat diffusion pearlite wet drawing microstructure necking fracture
  • 相关文献

参考文献14

二级参考文献54

  • 1陈家光,曹圣泉.低碳钢显微结构的EBSD表征[J].物理测试,2005,23(2):1-5. 被引量:10
  • 2郭泽尧,潘应君.82B高碳钢盘条拉拔脆断的原因分析[J].武汉船舶职业技术学院学报,2005,4(2):11-14. 被引量:9
  • 3龚桂仙,韩荣东,许竹桃.硬线盘条笔尖状断口断裂分析[J].武钢技术,2005,43(3):1-4. 被引量:13
  • 4亓奉友,陈戈萍,孙杰青.SWRH82B盘条脆断原因分析[J].金属制品,2005,31(6):28-29. 被引量:5
  • 5徐民奎.钢丝镀层与防腐[M].湘潭:湘潭钢铁公司职工大学,1988:74.
  • 6南田高明,平贺范明,柴田隆雄.ス-チル-コド用线材の步み.R.D神户制钢技报,2000,53(3):31.
  • 7徐效谦,阴绍芬.特殊钢丝生产.北京:冶金工业出版社,2001.
  • 8Languillaume J, Kapelski G, Baudelet B. Cementite dissolution in heavily cold drawn pearlite steel wires[ J ]. Acta Mater,1997,45 (3) :1201 -1212.
  • 9Read H G, Reynolds W T, Hono K, et al. APFIM and TEM studies of drawn pearlitic wire [ J ]. Scripta Materialia, 1997,37 (8) :1221 - 1230.
  • 10Hono K, Ohnuma M, Murayama M,et al. Cementite decomposition in heavily drawn pearlite steel wire[ J]. Scripta Mater,2001,44 (6) :977 -983.

共引文献97

同被引文献10

引证文献1

二级引证文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部