40MN锆挤压机挤压工艺研究 被引量:3

Study on extrusion process of zirconium alloy
下载PDF
导出
摘要 锆合金因其变形抗力大、流动性差、粘性强等特性,锆合金挤压过程中对挤压比、工模具形状、挤压速度、加热温度、润滑工艺等都有严格的要求。某40 MN 双动锆挤压机组生产某牌号核级锆材,采用专用润滑剂涂层润滑,坯锭的加热温度偏差控制在30℃左右,保温时间控制在10 min左右,采用扩孔挤压,扩孔速度控制在5~10 mm/s,挤压速度3~5 mm/s。达到锆合金挤压的最佳效果。 Zirconium alloy has properties of large deformation resistance,poor mobility,and strong viscosity. It leads strict requirements of extrusion ratio,mold shape,extrusion speed,heating temperature,and lubrication process.A 40 MN double-action zirconium extrusion is used to produce a grade of nuclear zirconium.Special lubricant is used for coating lubrication,heating temperature deviation of billet is controlled in about 30℃, holding time is controlled in about 10 min,reaming extrusion is selected,reaming speed is 5 ~10 mm/s,and extrusion speed is 5 ~10 mm/s.Precise result can be obtained in zirconium alloy extruding.
出处 《重型机械》 2015年第2期35-37,共3页 Heavy Machinery
基金 "高档数控机床与基础制造科技重大专项"资金支持项目(20092X04005-031)
关键词 锆合金 难变形金属 挤压工艺 zirconium alloy extrusion speed heating temperature extrusion process
  • 相关文献

参考文献11

二级参考文献111

共引文献248

同被引文献20

引证文献3

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部