摘要
通过抗弯强度测试研究了LiF和CaF2对陶瓷结合剂性能的影响.结果表明在Al-Si-O系陶瓷结合剂中,CaF2的析晶现象明显大于LiF.以LiF为助溶剂的陶瓷结合剂比用CaF2为助溶剂的陶瓷结合剂熔点低、粘接强度大.当以LiF为助熔剂时,可以用摩尔数比值（Al2O3+B2O3）/（R2O+RO+0.5LiF）判断陶瓷结合剂自身的强度.
The effects of LiF and CaF2 in the vitreous bond have been studied by the measurement of bonding strength. The results show that, the trend of CaF2 crystallization from Al-Si-O system vitreous bond is more obvious than that of LiF. The melting-point of the bonds is lower and the bonding force is stronger when using LiF than CaF2 as flux. The mole ratio (Al2O3+B2O3)/(R2O+RO+0.5LiF)can be used as a criterion to confirm the self-strength of the vitreous bonds.