某汽车车身耐腐蚀性试验 被引量:13

Corrosion Resistance Experiment of a Vehicle Body
下载PDF
导出
摘要 为验证某皮卡车型的防腐蚀性能,对该车进行了60个循环的整车强化腐蚀试验,分析了镀锌板、结构设计、打胶工艺对车身防腐蚀性能的影响。结果表明,镀锌板的防腐蚀性能明显优于非镀锌板,相同厚度的热镀锌板和电镀锌板的防腐蚀性能相当;A柱与翼子板间夹缝宽度小于0.1mm时,容易产生腐蚀,而当夹缝宽度大于0.2 mm时,则可以避免锈蚀现象;在钢板搭接位置适量涂覆焊缝密封胶,可保证6个腐蚀年(60个循环试验)不会出现腐蚀问题。本工作对各种腐蚀模态作了试验及理论的探索。 A 60-cycle vehicle accelerated corrosion test was performed to verify the corrosion performance of a pickup.And the effects of different body structures,glue process and galvanized sheet on the corrosion resistance were investigated.The results showed that corrosion resistance of galvanized sheet was better than that of non galvanized sheet,and there was no difference between hot dip galvanized sheet and galvanized sheet when the thickness was the same.Corrosion was more likely to occur when the gap between A-pillar and front wing was smaller than 0.1mm,but corrosion could be avoided when the gap was larger than 0.2mm.Appropriate amount of PVC sealant must be applied to welding seams to ensure sufficient corrosion resistance for 6 corrosion test years(60-cycle test).All the above corrosion modes were experimentally studied and theoretically explored in this research.
出处 《腐蚀与防护》 CAS 北大核心 2015年第4期366-368,372,共4页 Corrosion & Protection
关键词 车身 镀锌板 防腐蚀 vehicle body galvanized sheet conplate corrosion resistance
  • 相关文献

参考文献6

二级参考文献8

  • 1左景伊 金志强.腐蚀裂缝内分学和电化学状态之探索[J].化工学报,1982,33(4):290-301.
  • 2杨武 Pourbaix A.Cr和Mo对钢的局部腐蚀发展过程的影响[J].中国腐蚀与防护学报,1983,3(1):22-33.
  • 3赵景茂.碳钢在NaHCO3-NaCl体系中的局部腐蚀行为和机理研究,北京:北京化工大学学位论文[M].,2001..
  • 4胡茂圃,腐蚀电化学,1991年,217页
  • 5杨武,中国腐蚀与防护学报,1983年,3卷,1期,22页
  • 6左景伊,化工学报,1982年,33卷,4期,290页
  • 7陈卓,杜翠薇,曹备,吴荫顺,杨海,张峥嵘.碳钢缝隙内溶液化学和阳极极化行为研究[J].电化学,1999,5(2):145-151. 被引量:16
  • 8许淳淳,傅晓萍,刘幼平.几种无机阴离子的电迁移及其对闭塞区的影响[J].腐蚀科学与防护技术,2000,12(3):130-133. 被引量:10

共引文献64

同被引文献113

引证文献13

二级引证文献19

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部