高铬铁基药芯焊丝不同堆焊工艺下的显微组织与性能研究 被引量:4

Research of Microstructure and Properties of High Chromium Iron Based Flux-cored Wire Using Different Hardfacing Processes
下载PDF
导出
摘要 采用高铬铁基耐磨合金细粉做成药芯焊丝,分别用埋弧堆焊和等离子束堆焊方法制备耐磨试样,对试样的显微组织、硬度分布、耐磨性分别进行研究。实验表明:埋弧堆焊和等离子束堆焊组织具有较明显的区别,埋弧堆焊试样结晶定向性更好,晶粒更细化;埋弧堆焊涂层显微硬度平均值为791HV0.2,等离子束堆焊涂层显微硬度平均值为774HV0.2,埋弧堆焊涂层的显微硬度分布更均匀;耐干砂磨粒磨损性能埋弧堆焊是等离子束堆焊的1.7倍。 The wear-resistant samples were prepared by submerged arc hardfacing and plasma arc hardfacing process respectively using high chromium iron base alloy fine powder flux-cored wire.The microstructure,hardness distribution,wear resistance of the samples were studied respectively.The experiments show that the microstructure has a significant difference between the submerged arc hardfacing sample and the plasma arc hardfacing sample,crys-tallization stereospecificity of the submerged arc hardfacing sample is better,and its grain is refined;the average mi-crohardness of the submerged arc hardfacing sample is 791 HV0.2 ,the average microhardness of the plasma arc hard-facing sample is 774HV0.2 ,the submerged arc hardfacing sample has more uniform microhardness distribution;the dry sand abrasive wear resistance of the submerged arc hardfacing sample is about 1.7 multiples that of the plasma arc hardfacing sample.
出处 《材料导报》 EI CAS CSCD 北大核心 2015年第12期110-113,共4页 Materials Reports
基金 青岛市科技发展计划(12-1-4-6-(4)-jch) 青岛市技术创新平台建设计划(14-7-2-42-gx) 青岛经济技术开发区重点科技发展计划(2013-1-51) 山东科技大学科研创新团队支持计划 国家级大学生创新创业训练计划
关键词 埋弧堆焊 等离子束堆焊 高铬铁基药芯焊丝 显微组织 耐磨性能 submerged arc hardfacing plasma arc hardfacing high chromium iron based flux-cored wire mi-crohardness wear-resistant property
  • 相关文献

参考文献9

二级参考文献32

共引文献158

同被引文献19

引证文献4

二级引证文献6

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部