快速凝固Al-Fe-Ce合金的相变与性能研究 被引量:4

Study on Phase Transition and Mechanical Properties of Rapidly Solidified Al-Fe-Ce Alloy
下载PDF
导出
摘要 采用相成分分析(X射线衍射)、组织观察(透射电子显微镜)和力学性能检测(显微硬度)等结合的方法,对单辊旋铸法制备的快速凝固Al-6.87Fe-3.95Ce合金薄带的急冷态和退火态进行相变与热稳定性能的分析.亚稳相Al_(10)Fe_2Ce和平衡相Al_(13)Fe_3Ce的晶格参数以及晶格结构已被确定.棒状的亚稳相Al_(20)Fe5Ce也在TEM中被观察到.稳定相Al_(13)Fe_3Ce是亚稳相Al_(10)Fe_2Ce和Al_(20)Fe5Ce经过热处理后不完全转变而形成.结果表明:在退火处理过程中,随着温度的升高,有明显的析出相出现,并且出现了长大趋势;显微硬度也随退火温度变化而变化,在340℃出现最高峰值,说明该合金在340℃能保持较好的热稳定性. In the paper the phase transition properties and thermostability of rapidly solidified A1-6.87Fe-3.95Ce alloy strip prepared by single roller casting in rapidly quenched state and annealing state were investigated by using X-ray diffraction(XRD), transmission electron microscopy (TEM), and microhardness test. Lattice parameters and structures of metastable Al10 Fez Ce phase and equilibrium Al13 Fe3 Ce phase were identified. Bar-shaped metastable Al20 Fe5 Ce phase was observed in TEM. Stable Al13 Fe3 Ce phase was the incomplete transformation of metastable Al10 FezCe phase and A120 FesCe phase after heat treating. The results showed that distinct precipitated phase appeared and grew with the increase of temperature during annealing treatment; Microhardness changed with annealing temperature and reached a peak value at 340 ℃, at which temperature the alloy had good thermostability.
出处 《上海有色金属》 CAS 2015年第4期148-152,共5页 Shanghai Nonferrous Metals
关键词 Al-Fe-Ce合金 快速凝固 退火处理 显微硬度 相变 Al- Fe- Ce alloy rapidly solidify annealing treatment microhardness phasetransition
  • 相关文献

参考文献14

  • 1贺毅强,徐政坤,陈振华.快速凝固Al-Fe系耐热铝合金的研究进展[J].材料科学与工程学报,2011,29(4):633-638. 被引量:11
  • 2Thursfield G, Stowell M J. Mechanical properties of A1-8 wt% Fe-based alloys prepared by rapid quenching from the liquid state [J]. Journal of Material Science, 1974, 9 (10) : 1644 - 1660.
  • 3Skinner DJ,Bye R L, Raybould D, et al. Dispersion strengthened A1- Fe- V- Si alloys[J]. Seripta Metallurgica, 1986,20(6) :867 - 872.
  • 4Skinner D J. The physical metallurgy of dispersion strengthened AI- Fe- V- Si alloys[M]. Kim Y W, Griffith W M. Dispersion strengthened aluminum alloys. Warrendale, PA: the Mineral Metal and Materials Society, 1988:181- 197.
  • 5Griffith W M, Somders R E, Hildman G J. Elevated temperature aluminium alloys for aerospace application [J ]. High-S~ Povrder Metallm'gy AI Alloys, 1982,209- 224.
  • 6Skinner D J, Okazaki K, Adam C M. Rapid solidified powder aluminum alloys[M]. Fine M E, Starke Jr A E. ASTM-STP 890. Philadelphia, PA: ASTM, 1985.
  • 7Jones H. Prediction versus experimental fact in the formation of rapidly solidified microstructure [J]. ISIJ International, 1995,35 (6) : 751 - 756.
  • 8ASM International Handbook Committee. Metals Hand book' Volume 2 [M]. 10th ed. Warrendale: ASM International, 1990.
  • 9Couper M J, Luster J W, Thumann M. Development of elevated temperature powder metallurgy aluminum alloys [J]. Metallurgy Powder International, 1991,23 ( 1 ) : 7 - 15.
  • 10李沛勇,戴圣龙,于海军.快速凝固/粉末冶金铝合金的研究进展和应用前景[c].全国第一届铝合金及其应用会议.陇西:中国有色金属会,2003.

二级参考文献76

共引文献42

同被引文献72

引证文献4

二级引证文献26

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部