真空热处理对激光近净成形In625和C-276合金性能的影响 被引量:4

Influence of Vacuum Heat Treatment on Properties of Laser Engineered Net Shaping In625 and C-276 Alloy
下载PDF
导出
摘要 对激光近净成形两种镍基高温合金Inconel 625和Hastelloy C-276分别进行热处理实验,然后分析热处理工艺参数对合金室温拉伸性能的影响。结果分析表明:在800,900℃去应力热处理后,Inconel 625合金抗拉强度提升不明显,而在1000℃以上进行固溶处理后,合金抗拉强度得到提高。1100℃热处理后,Inconel 625合金的抗拉强度与沉积态相比得到明显提高。在800,900℃去应力热处理后,Hastelloy C-276合金强度也未明显提高,而在1000℃以上进行热处理,随着热处理温度提高,合金抗拉强度逐渐升高。1150℃进行热处理后,Hastelloy C-276合金的抗拉强度与沉积态相比得到明显提高。激光近净成形工艺制备的两种镍基高温合金室温拉伸断裂方式为韧性断裂。 The heat treatment of laser engineered net shaping two kinds of nickel-based superalloy was carried out,and the influence of heat treatment parameters to the alloy's property was analyzed.The analysis of results indicates that:the room temperature tensile strength of Inconel 625 superalloy is not improved obviously under the stress relieving heat treatment,nevertheless after the solution treatment is done over 1000℃,the room temperature tensile strength is improved.The tensile strength after 1100℃ heat treatment is improved obviously compared with the deposited condition.The room temperature strength of Hastelloy C-276 is not improved obviously under the stress relieving heat treatment.Whereas,when the heat treatment is done above 1000℃,the room temperature tensile strength of laser near net shaping Hastelloy C-276 superalloy gradually increases with the increase of heat treatment temperature.After 1150℃ heat treatment,the tensile strength of Hastelloy C-276 increases obviously,compared with the deposited condition.The fracture mode of the two kinds of laser engineered net shaping nickel-based superalloy is ductile fracture.
出处 《材料工程》 EI CAS CSCD 北大核心 2016年第3期28-34,共7页 Journal of Materials Engineering
基金 中科院重点部署项目(KGZD-EW-T04-2)
关键词 镍基高温合金 激光近净成形 热处理 力学性能 nickel-based superalloy laser engineered net shaping heat treatment mechanical property
  • 相关文献

参考文献17

二级参考文献158

共引文献268

同被引文献36

引证文献4

二级引证文献15

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部