HX_D3型电力机车SEA107型牵引电机NU330轴承内套出现裂纹的原因分析

Cause Analysis of NU330 Bearing Inner Sleeve Crack of SEA107 Traction Motor for HX_D3 Electric Locomotive
下载PDF
导出
摘要 对洛阳机务段HX_D3机车牵引电机NU330轴承运用中的问题进行了调查,对调查中还未出现故障的轴承内套滚道面出现的初始裂纹进行了全面材料检验,分析认为该轴承早期失效的原因是轴承内圈滚道面局部承受了较高的接触应力所致。 In this paper,the traction motor NU330 bearings' application problems of HX_D3 electric locomotives allocated in Luoyang Locomotive Depot are investigated,the comprehensive material inspection is conducted for the initial crack of no-fault bearings inner raceway surface,and the cause of bearing premature failure is confirmed that the bearing inner ring raceway surface has suffered higher contact stress.
作者 李霞
出处 《铁道机车车辆》 2016年第2期67-69,共3页 Railway Locomotive & Car
关键词 HXD3型电力机车 NU330轴承 内圈 裂纹 原因分析 HXD3electric locomotive NU330bearing inner ring crack cause analysis
  • 相关文献

参考文献6

  • 1张曙光.HX.,3型电力机车[M].北京:中国铁道出版社,2010.
  • 2龙洙,权中太.铁路机车滚动轴承手册[M].北京:中国铁道出版社,1995.
  • 3GB/T4336-2002碳素钢和中低合金钢火花源原子发射光谱分析方法[S].
  • 4GB/T230.1-2009.金属材料洛氏硬度试验[S].
  • 5JB/T1255-2001.高碳铬轴承钢滚动轴承零件热处理技术条件[S].[S].,..
  • 6GB/T18254-2002.高碳铬轴承钢[S].[S].,..

共引文献31

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部