摘要
在氯盐环境中进行纤维掺量为1%和2%的PVA纤维增强水泥基增强复合材料(简称PVA-FRCC)温度+干湿循环的试验,以Fick第二定律为基础,建立考虑温度因素的理论模型,并利用最小二乘法优化得到氯离子扩散系数。结果表明:氯离子扩散系数随试验周期的增加而减小,而温度的增加会减弱试验周期对氯离子扩散系数的影响;相同温度作用下两种纤维掺量的试件,氯离子扩散系数差距不明显。
The frost resistance of polyvinyl alcohol fiber reinforced cementitious composites （ PVA - FRCC ） in chloride environment was conducted a wet -dry cycle test at different temperatures.Influence of temperature on chloride diffusion depth,chloride concentration, chloride diffusion coefficient, the results show that the PVA - ECC specimens in chloride environment, temperature on concentration,chloride diffusion coefficient has a positive impact,and the higher the temperature,the greater the impact,chloride diffusion coefficient decreasing with increases of wet - dry cycle, while with the increase in temperature will lead to affect the wet - dry cycle for chlo- ride diffusion coefficient of waning.
出处
《混凝土》
CAS
北大核心
2016年第4期36-38,共3页
Concrete
基金
国家自然科学基金(51368041
51168033)
内蒙古自然科学基金(2012MS0706
2013MS0709)
内蒙古自治区高等学校科学研究项目(NJZY13104)
关键词
水泥基复合材料
聚乙烯醇纤维
氯盐环境
干湿循环
温度
氯离子扩散系数
engineered cementitious composite
polyvinyl alcohol fiber
chloride environment
wet - dry cycle
temperature
chloride diffusion coefficient