针对目前我国低品位菱镁矿利用率低下的现状,提出了对低品位菱镁矿进行开发利用的设想,以辽宁海城低品位菱镁矿为研究对象,对其进行了水化试验研究。通过检测水化过程中低品位菱镁矿中Mg^(2+)的水化率及其反应过程中镁元素物相变化这两个指标,分别对低品位菱镁矿水化过程的影响因素进行了试验研究。研究结果表明,在低品位菱镁矿粒度-0.074 mm、反应物料固液比1∶49、反应温度80℃、反应时间50 min的条件下,低品位菱镁矿的水化率高达92.0%,该研究结果为后续低品位菱镁矿的提纯提供试验依据。
Aimed at the low utilization rate of low grade magnesite in china,the writer puts forward the assumption to exploit it. In the article, low grade magnesite from Haicheng Liaoning Province is researched on hydration test. And hydration rate as well as phase change of Mg2 ＋are the targets for observing influencing factors in hydration process. Result shows that hydration rate of low grade magnesite is up to 92. 0% with grain size- 0. 074 mm,reactants liquid to solid ratio 1 ∶ 49,temperature 80 ℃degree,reaction time for 50 min. The experiment will provide test basis for the subsequent purification of low grade magnesite.
出处
《硅酸盐通报》
CAS
CSCD
北大核心
2016年第4期1096-1100,共5页
Bulletin of the Chinese Ceramic Society
基金
国家自然科学青年基金(51004064
51204091)
辽宁省高等学校优秀人才支持计划项目(LJQ2014035)
关键词
低品位菱镁矿
水化率
影响因素
low grade magnesite
hydration rate
influencing factors