22MnB5钢三种热冲压成形件的冷弯性能 被引量:9

Cold Bending Properties of Three Kinds of 22MnB5Steel Hot Stamping Parts
下载PDF
导出
摘要 从汽车用22MnB5钢三种热冲压成形件(国产A柱、进口B柱和用进口钢板生产的防撞杆)上制取不同宽度的冷弯试样(试样的最小宽度至少为板厚的20倍)和非标拉伸试样,按照德国标准VDA 238-100进行弯曲试验,比较了三种热成形件的冷弯性能;此外还进行了拉伸试验,并观察了拉伸断口和弯曲断口的形貌。结果表明:三种热成形件的组织均为板条马氏体,它们的拉伸性能相当,拉伸断口均分为三个区,即纤维区、放射区和剪切唇,放射区为少见的条带状;三种热成形件的弯曲角度相近,均小于60°,冷弯性能相当,这与它们的显微组织相同有关;弯曲断口形貌呈不同形态的韧窝。 The bending samples with various width and non-standard tensile samples were cut from three kinds of 22MnB5 steel hot stamping parts (domestic A pillar, impute B pillar and door beam made from impute steel plate), the width of bending sample should be more than 20 times thickness. Bending test was carried out according to German standard VDA 238-100, and cold bending properties of various hot stamping parts were compared. In addition, tensile test was carried out, and tensile fracture morphology and bending fracture morphology were observed. The results show that the microstructure of three kinds of hot stamping parts all were lath martensite, their tensile properties were about the same. Tensile fracture can divide three domain: fiber area, radical area and shear lip. The radical zone is infrequent strip and band structure. The measured bending angles of three hot stamping parts were about the same and less than 60°, this related to their same microstructure. The morphology of fracture for bending samples was dimple structure with different morphology.
出处 《机械工程材料》 CAS CSCD 北大核心 2016年第7期7-12,共6页 Materials For Mechanical Engineering
关键词 热冲压成形件 冷弯性能 显微组织 断口形貌 22MnB5钢 hot stamping parts cold bending property microstructure fracture morphology 22MnB5 steel
  • 相关文献

参考文献5

  • 1马鸣图,路洪洲,李志刚.汽车轻量化和高强度钢的先进的加工成形技术[C]//机械装备结构材料与表面技术研讨会论文集.兰州:中国机械工程学会,2009:467-473.
  • 2MA Ming-tu, ZHANG Yi-sheng, SONG l.ei-feng, Research and progress of hot stamping in China et al. [C]// Advanced Materials Research. Switzerland : Trans Tech Publications, 2015: 151-168.
  • 3LEE J H, CHO Y R, CHOO S D. Investigation of tensile properties and hendability of CMnB hot-press forming steel [C]//4th International Conference Proceedings of Hot Sheet Metal Forming of High-Performance Steel. Lulea: [s. n.], 2013:547-556.
  • 4徐祖耀.马氏体相变和马氏体[M].北京:科学出版社,1980.87.
  • 5靳海亮,赵爱民,陈银莉,程俊业.钛对含硼热冲压成形用钢组织和性能的影响[J].机械工程材料,2012,36(8):6-9. 被引量:4

二级参考文献7

  • 1江海涛,唐荻,米振莉.汽车用先进高强度钢的开发及应用进展[J].钢铁研究学报,2007,19(8):1-6. 被引量:108
  • 2褚幼义 贺信莱 唐立 等.硼在奥氏体晶界的两类偏聚.金属学报,1987,23(3):169-174.
  • 3KLEINER M, GEIGER M, KLAUS A. Manufacturing of light- weight components by metal forming[J].CIRP Annals Manu- facturing Technology, 2003,52(2) : 521-542.
  • 4NADERI M, KETABCHI M, ABBSI M, et al. Analysis of microstructure and mechanical properties of different hot stamped B-bearing steels [J]. Steel Research Int. 2010,81 ( 3 ) : 216-223.
  • 5MYOUNG-GYU L, SUNG-JOON K. Application of hot pressforming process to manufacture an automotive part and its finite element analysis considering phase transformation plas- ticity[J]. International Journal of Mechanical Sciences, 2009, 51 : 888-898.
  • 6NADERI M,SAEEINAKBARI A, BLECK,W. The effects of non-isothermal deformation on martensitic transformation in 22MnB5 steel[J]. Materials Science and Engineering A, 2008, 487 : 445-455.
  • 7TURETTA A, BRUSCHI S, GHIOTTI A. Investigation of 22MnB5 formability in hot stamping operations[J]. Journal of Materials Processing Technology, 2006,177:396-400.

共引文献6

同被引文献67

引证文献9

二级引证文献56

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部