Effects of sliding velocity and normal load on tribological behavior of aged Al-Sn-Cu alloy

摩擦速度和加载载荷对时效态Al-Sn-Cu合金摩擦磨损性能的影响(英文)
下载PDF
导出
摘要 The tribological behavior of aged Al-Sn-Cu alloy rubbed in the presence of lubricant over a range of sliding velocities and normal loads was investigated. The results showed that peak-aged (PA) alloy had a better tribological behavior than under-aged (UA) and over-aged (OA) alloys, which could be attributed to the optimized strength-ductility matching and a better hardness under PA condition. Wear rate and friction coefficient showed great sensitivity to applied sliding velocity and normal load. The wear rate and friction coefficient of the alloy exhibited a reduction trend with the increase in sliding velocity. The low wear rate and friction coefficient of alloy at high velocities were due to the effectively protected film and homogeneous Sn on surface. However, an increase in normal load led to an obvious increment in wear rate. The friction coefficient exhibited a fluctuant trend with the increase of normal loads. The seriously destroyed film and abraded Sn resulted in poor tribological behavior at high normal loads. The Sn particles and lubricant film which includes low shear interfacial lubricating layer and oxide tribolayer are the key to the tribological behavior of Al-Sn-Cu alloy. 研究在油润滑状态下摩擦速度和加载载荷对时效态Al-Sn-Cu合金摩擦磨损性能的影响。结果表明:由于峰时效合金较欠时效和过时效合金具有最佳的强度-塑性配比和更高的硬度,因此峰时效合金表现出最优的摩擦磨损性能。摩擦速度和加载载荷对合金磨损率和摩擦因数具有显著影响。随着摩擦速度的增大,磨损表面的润滑膜和Sn相更为均匀,合金的磨损率和摩擦因数均降低;然而随着加载载荷的增加,均匀的润滑膜和Sn相被严重破坏,合金磨损率急剧上升。Sn相和包括中间润滑层、摩擦氧化层的润滑膜是影响Al-Sn-Cu合金摩擦磨损性能的决定性因素。
出处 《Transactions of Nonferrous Metals Society of China》 SCIE EI CAS CSCD 2016年第7期1809-1819,共11页 中国有色金属学报(英文版)
基金 Project(2013AH100055)supported by the Special Foundation for Science and Technology Innovation of Foshan,China
关键词 Al-Sn-Cu alloy tribological behavior sliding velocity normal load AGING Al-Sn-Cu合金 摩擦磨损性能 摩擦速度 加载载荷 时效
  • 相关文献

参考文献46

  • 1üNLü B S, DURMUS H, AKGüN S. Tribological and mechanical properties of Al alloyed bearings [J]. Journal of Alloys and Compounds, 2009, 487: 225-230.
  • 2PATHAK J P, MOHAN S. Tribological behaviour of conventional Al-Sn and equivalent Al-Pb alloys under lubrication [J]. Bulletin of Materials Science, 2003, 263: 15-320.
  • 3LIU X, ZENG M Q, MA Y, ZHU M. Wear behavior of Al-Sn alloys with different distribution of Sn dispersoids manipulated by mechanical alloying and sintering [J]. Wear, 2008, 265: 1857-1863.
  • 4BRAVO A E, DURAN H A, JACOBO V H, ORTIZ A, SCHOUWENAARS R. Towards new formulations for journal bearing alloys [J]. Wear, 2013, 302: 1528-1535.
  • 5LIU X, ZENG M Q, MA Y, ZHU M. Promoting the high load-carrying capability of Al-20wt%Sn bearing alloys through creating nanocomposite structure by mechanical alloying [J]. Wear, 2012, 294-295: 387-394.
  • 6KOTADIA H R, DAS A, DOERNBERG E, SCHMID-FETZER R. A comparative study of ternary Al-Sn-Cu immiscible alloys prepared by conventional casting and casting under high-intensity ultrasonic irradiation [J]. Materials Chemistry and Physics, 2011, 131: 241-249.
  • 7YAN N, HONG Z Y, GENG D L, WANG W L, WEI B. Phase separation and structure evolution of ternary Al.Cu.Sn immiscible alloy under ultrasonic levitation condition [J]. Journal of Alloys and Compounds, 2012, 544: 6.12.
  • 8PRAMANICK A, CHATTERJEE S, BHATTACHARYA V, CHATTOPADHYAY K. Synthesis and microstructure of laser surface alloyed Al.Sn.Si layer on commercial aluminum substrate [J]. Journal of Materials Research, 2005, 20: 1580.1589.
  • 9PERRONE A, ZOCCO A, ROSA H D, ZIMMERMANN R, BERSANI M. Al.Sn thin films deposited by pulsed laser ablation [J]. Materials Science and Engineering C, 2002, 22: 465.468.
  • 10UEDA M, INABA R, OHTSUKA T. Composition and structure of Al.Sn alloys formed by constant potential electrolysis in an AlCl3.NaCl.KCl.SnCl2 molten salt [J]. Electrochimica Acta, 2013, 100: 281.284.

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部