摘要
The effect of adding 0.5mass% Cu on ductility and magnetic properties of Fe-6.5Si（mass%）alloy was investigated.The alloys with and without 0.5mass% Cu addition were warm rolled into thin sheets of thickness no more than 0.3mm at temperature below 600 ℃.It was found that the alloy with 0.5mass% Cu addition was more easily warm rolled than Cu-free alloy.Tensile tests were carried out to further investigate this phenomenon,which confirmed that the ductility of the alloy with 0.5mass% Cu addition was significantly higher than that of Cu-free alloy at 550 ℃.Based on the results of transmission electron microscopy analysis,the ductility increase of the alloy with 0.5mass% Cu addition was attributed to the effect of Cu on the promotion of dynamic recovery and suppression of long-range order in the alloy during warm rolling process.It was also observed that the iron loss was lower and inductance was higher for the alloy with 0.5 mass% Cu addition.Thus,it can be concluded that adding a suitably small amount of Cu would not only increase the ductility of Fe-6.5Si alloy at warm rolling temperatures but also improve its magnetic properties.
The effect of adding 0.5mass% Cu on ductility and magnetic properties of Fe-6.5Si（mass%）alloy was investigated.The alloys with and without 0.5mass% Cu addition were warm rolled into thin sheets of thickness no more than 0.3mm at temperature below 600 ℃.It was found that the alloy with 0.5mass% Cu addition was more easily warm rolled than Cu-free alloy.Tensile tests were carried out to further investigate this phenomenon,which confirmed that the ductility of the alloy with 0.5mass% Cu addition was significantly higher than that of Cu-free alloy at 550 ℃.Based on the results of transmission electron microscopy analysis,the ductility increase of the alloy with 0.5mass% Cu addition was attributed to the effect of Cu on the promotion of dynamic recovery and suppression of long-range order in the alloy during warm rolling process.It was also observed that the iron loss was lower and inductance was higher for the alloy with 0.5 mass% Cu addition.Thus,it can be concluded that adding a suitably small amount of Cu would not only increase the ductility of Fe-6.5Si alloy at warm rolling temperatures but also improve its magnetic properties.
基金
Item Sponsored by Natural Science Foundation of Hubei Province of China(2008CDA040)