成核剂TMC-210对聚乳酸结晶及性能的影响 被引量:5

Influence of Nucleator TMC-210 on Crystallization and Properties of PLLA
下载PDF
导出
摘要 针对聚乳酸结晶速率慢和冲击强度低的问题,考察了熔融共混添加成核剂TMC-210对PLLA结晶、熔融行为和力学性能的影响。研究发现,纯L-聚乳酸(PLLA)在10℃/min降温过程中不结晶,当TMC-210质量分数为0.2%时,PLLA就能显著结晶,并且随着TMC-210含量的增加,结晶峰移向高温。从等温结晶结果看,TMC-210的添加使得PLLA结晶时间缩短,结晶速率加快。另外,PLLA的成核密度增加且球晶尺寸减小,同时,TMC-210质量分数为0.2%时,PLLA的冲击强度提高了3.3倍。因此,添加TMC-210是一种能够促进PLLA结晶和增韧的有效成核剂。 In order to solve the problem of slow crystallization rate and low impact strength,the nucleating agent TMC-210 was introduced into poly( L-lactic acid)( PLLA) via melt blend. The effects of TMC-210 on crystallization,melting behavior,and mechanical properties of PLLA were investigated. It is found that pure PLLA has no crystallization peak upon cooling at 10 ℃ / min. However,with loading 0. 2% TMC-210,PLLA can complete crystallization,and the crystallization peak shifts to higher temperature with increasing the TMC-210 content. Isothermal crystallization analysis reveals that the addition of TMC-210 leads to shorter crystallization time and faster crystallization rate of PLLA. Besides,the nucleation density of PLLA increases and the spherulite size decreases. When the TMC-210 mass fraction is 0. 2%,the impact strength of PLLA is enhanced by 3. 3 times. Therefore,adding nucleating agent TMC-210 is an effective approach to promote the crystallization rate and impact strength of PLLA.
出处 《高分子材料科学与工程》 EI CAS CSCD 北大核心 2016年第10期66-72,共7页 Polymer Materials Science & Engineering
基金 国家自然科学基金资助项目(21264012)
关键词 聚乳酸 结晶 冲击强度 TMC-210 poly(L-lactic acid) crystallization impact strength TMC-210
  • 相关文献

参考文献3

二级参考文献18

  • 1钱欣,田怡.聚乙二醇增塑聚乳酸的等温结晶动力学研究[J].塑料工业,2006,34(B05):221-223. 被引量:9
  • 2李春,辛忠,乔绪明,李琳.取代芳基磷酸金属盐类成核剂对聚乳酸结晶的影响[J].中国塑料,2006,20(10):79-82. 被引量:26
  • 3任杰,杨军,任天斌.生物可降解材料聚乳酸结晶行为研究进展[J].高分子通报,2006(12):51-56. 被引量:32
  • 4吴亮,吴德峰,吴兰峰,张明.聚乳酸/蒙脱土纳米复合材料的冷结晶及熔融行为[J].高分子材料科学与工程,2007,23(5):124-127. 被引量:35
  • 5Auras R, Harte B, Selke S. An Overview of Polylactides as Packagingmaterials [ J ]. Macromolecular Bioscience 2004,4(9) :835 -64.
  • 6Harris AM, Lee EC. Improving Mechanical Perform- ance of Injectionmolded PLA by Controlling Crystallini- ty [ J ]. Journal of Applied PolymerSeience 2008,107 (4) :2246 - 55.
  • 7Perego G, Cella GD, Bastioli C. Effect of Molecular Weight Andcrystallinity on Poly(lactic acid) Mechani- cal properties [ J ]. Journal of Applied Polymer Science 1996,59( 1 ) :37 -43.
  • 8Drieskens M, Peeters R, Mullens J, et al. Structure ver- sus Properties Relationship of Poly (lacticacid). I. Effect of Crystallinity on Barrier Properties [ J ]. Journal of Polymer Science Part B:Polymer Physics 2009,47 (22) :2247-58.
  • 9R. E.Drumright,P. R.Gruber,D. E.Henton.Polylactic Acid Technology[J].Adv Mater.2000(23)
  • 10Eamor M. Woo,Ling Chang.Crystallization and morphology of stereocomplexes in nonequimolar mixtures of poly( l -lactic acid) with excess poly( d -lactic acid)[J].Polymer.2011(26)

共引文献28

同被引文献58

引证文献5

二级引证文献22

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部