摘要
采用真空半固态搅拌铸造法制备40%（体积分数）的高含量SiCp/A356复合材料;然后以40%SiCp/A356复合材料为原料,采用“稀释法”分别制备出体积分数10%、20%、30%衍生SiCp/A356复合材料。通过对比分析高体积含量复合材料稀释制备的衍生复合材料（衍生材料）与直接搅拌制备的搅拌SiCp/A356复合材料（搅拌材料）的断口形貌,发现衍生材料的断口质量及颗粒分布均匀程度均优于相同颗粒含量搅拌材料的;不同颗粒含量的孔隙率、布氏硬度、力学性能变化规律具有稀释效应,即颗粒含量越低,对应数值越小;相同颗粒含量衍生材料的硬度比搅拌材料的高3%～5%左右,力学性能比搅拌材料的力学性能高9%～13%。
SiCp/A356 composites with high content of 40% （volume content） were prepared by vacuum semi-solid stirring method, and the derived composites with 10%, 20%, 30% （volume content） particle content were prepared by dilution method with 40% （volume content） composites. By comparing the derived materials prepared by dilution of high content composites with the stirred material, prepared by direct stirring casting, it is found that the macroscopic fracture surface quality and particle distribution of the derived material are better than those of stirred material with the same particle size. The porosity, hardness and mechanical properties of the different particle content have dilution effect, that is, the lower the particle content, the smaller the corresponding value. The hardness of derived material is 3%-5% higher than that of the stirred material, and the mechanical properties of derived material are 9%-13% higher than those of the stirred material at the same SiC content.
出处
《中国有色金属学报》
EI
CAS
CSCD
北大核心
2016年第10期2078-2085,共8页
The Chinese Journal of Nonferrous Metals
基金
国家"十二五"科技支撑计划资助项目(2015BAG12B01-09)
国家自然科学基金资助项目(51371022
51271014)
北京交通大学基本科研业务费资助项目(2015JBM076)~~