航空碳纤维树脂基复合材料加筋板压缩屈曲及后屈曲性能 被引量:6

Buckling and post-buckling performance of aeronautic carbon fiber reinforced resin composite stiffened panel under compression
原文传递
导出
摘要 开展了复合材料加筋板轴压稳定性实验,对加筋板的屈曲及后屈曲性能、破坏模式和后屈曲失效表征进行了研究.实验结果表明加筋板在轴压下具有良好后屈曲承载潜能,破坏载荷约为屈曲载荷的2.2倍;其屈曲模式为筋条间蒙皮首先发生屈曲失稳,筋条在整个承载过程中保持直线,起到"屈曲分隔"的作用.通过对加筋板屈曲及后屈曲性能的理论分析,得出的理论屈曲载荷和理论破坏载荷与实验结果相对误差均小于8%,并确定了在后屈曲过程中蒙皮中心挠度的变化规律和轴向载荷的面内分布特征. Compressive experiments on aero composite stiffened panel were conducted to study the carrying capacity,failure modes and post-buckling failure characterization.The results showed that the composite stiffened panel had a high post-buckling carrying capacity.The failure load was almost 2.2times of the buckling load.The skin bay initiated buckling first.However,the stiffeners had no buckling before failure,which worked as‘skin buckling separated'.According to the theoretical analysis,theoretical buckling and failure load had an error less than 8% compared with the experimental results.Additionally,the variation of the out-of-plane displacement on skin center and distribution of the axial compressive load were determined in the post-buckling process.
出处 《航空动力学报》 EI CAS CSCD 北大核心 2016年第10期2359-2369,共11页 Journal of Aerospace Power
关键词 复合材料加筋板 屈曲 后屈曲 破坏模式 理论分析 composite stiffened panel buckling post-buckling failure mode theoretical analysis
  • 相关文献

参考文献8

二级参考文献82

共引文献94

同被引文献59

引证文献6

二级引证文献29

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部