多轴向玻璃纤维增强树脂基复合材料的破坏特性和损伤机制 被引量:12

Failure behavior and damage mechanism of multiaxial glass fiber reinforced resin matrix composites
原文传递
导出
摘要 通过对玻纤增强环氧乙烯基酯树脂(GF/EVE)和玻璃纤维增强不饱和聚酯树脂(GF/UP)复合材料的多轴向铺层设计试件进行低速冲击、弯曲和剪切破坏性力学试验,分析了不同铺层方式的GF/EVE和GF/UP复合材料冲击、弯曲和剪切载荷作用下产生的损伤及失效模式。结果表明:在铺层设计与工艺相同的情况下,CF/EVE的弯曲强度、冲击韧性均优于CF/UP;[0,90]6试件冲击能量吸收性能优于其他五种铺层方式;铺设角设计、树脂基体类型、铺层厚度对层合板剪切力学性能的影响较小。并基于SEM与超声C扫描成像检测(C-SAM)对复合材料的微观界面脱粘机制及损伤演化行为进行阐释。 The experimental investigation on mechanical properties of the multi axial glass fiber reinforced epoxy vinyl ester resin(GF/EVE)and glass fiber reinforced unsaturated polyester(GF/UP)resin composite material were carried out.And the bending strength,interlaminar shear strength and modulus of the specimens were analyzed.The results show that,in the same layer design and process,the bending strength and impact toughness of GF/EVE resin are superior to GF/UP resin.[0,90]6specimen impact energy absorption performance is superior to the other five layer mode.And basing on SEM and micro ultrasonic C-scan imaging detection,the mechanism of the composites interface debonding mechanism and damage evolution behavior were elucidated.
出处 《复合材料学报》 EI CAS CSCD 北大核心 2017年第2期381-388,共8页 Acta Materiae Compositae Sinica
基金 国家自然科学基金(51465055) 新疆维吾尔自治区自然科学基金(2014211A010) 机械制造国家重点实验室开放课题(Sklms2014005)
关键词 玻纤 树脂 复合材料 冲击损伤 界面脱粘机制 glass fiber resin composites impact damage interface debonding mechanism
  • 相关文献

参考文献6

二级参考文献59

共引文献76

同被引文献84

引证文献12

二级引证文献44

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部