Production of low-silicon molten iron from high-silica hematite using biochar

Production of low-silicon molten iron from high-silica hematite using biochar
原文传递
导出
摘要 A new method of utilizing high-silica hematite to produce low-silicon molten iron was proposed.In this method,FASTMELT,which comprised direct reduction and melt separation processes,was applied,with highly reactive biochar as the reductant in the direct reduction stage.The proposed method was experimentally investigated and the results show that the method is feasible.In the direct reduction stage,ore-char briquette could achieve a metallization rate of 84%-88% and residual carbon of 0.27-0.89mass% at temperature of 1373 K,biochar mixing ratio of 0.8-0.9,and reduction time of 15 min.Some silica particles remained embedded in the iron phase after the reduction.In the melting separation stage,molten iron with a carbon content of 0.02-0.03mass% and silicon content of 0.02-0.18mass%could be obtained from the metallic briquettes under the above-mentioned conditions;the iron recovery rate was83%-91% and impurities in the obtained metal were negligible. A new method of utilizing high-silica hematite to produce low-silicon molten iron was proposed.In this method,FASTMELT,which comprised direct reduction and melt separation processes,was applied,with highly reactive biochar as the reductant in the direct reduction stage.The proposed method was experimentally investigated and the results show that the method is feasible.In the direct reduction stage,ore-char briquette could achieve a metallization rate of 84%-88% and residual carbon of 0.27-0.89mass% at temperature of 1373 K,biochar mixing ratio of 0.8-0.9,and reduction time of 15 min.Some silica particles remained embedded in the iron phase after the reduction.In the melting separation stage,molten iron with a carbon content of 0.02-0.03mass% and silicon content of 0.02-0.18mass%could be obtained from the metallic briquettes under the above-mentioned conditions;the iron recovery rate was83%-91% and impurities in the obtained metal were negligible.
出处 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2017年第1期27-33,共7页
基金 the National Natural Science Foundation of China(Grant No.51144010)for the financial support
关键词 High-silica hematite Low-silicon molten iron BIOCHAR Direct reduction Melt separation High-silica hematite Low-silicon molten iron Biochar Direct reduction Melt separation
  • 相关文献

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部