摘要
采用Gleeble-1500热模拟试验机,在变形温度300~500℃、应变速率0.000 1~0.01 s^(-1)的变形条件下,对SiC颗粒增强7090铝基复合材料进行等温恒应变速率热压缩试验,对热变形行为及微观组织进行研究。结果表明:流变应力的大小与位错在SiC颗粒处的堆积程度有关;随着温度的降低或应变速率的升高,堆积程度越大,使得流变应力增大;当温度为300℃、应变速率为0.01 s^(-1)时,峰值应力达到最大为153.6 MPa;复合材料热压缩后SiC颗粒分布更加均匀;变形温度升高或应变速率降低都会使再结晶晶粒增大。
The hot compressive tests of SiCp/7090A1 composites was investigated at temperatures from 300 ℃ to 500 ℃ and strain rates from 0.000 1 s^-1 to 0.01 s^-1 on Gleeble-1500 thermal simulation machine. With the increase of temperature reduction or strain rate, the degree of dislocation augment in SiC particles location. Peak stress at the maximum when temperature is 300 ℃ and the strain rate of 0.01 s^-1. SiC particle size distribution more uniform after hot compression. The recrystallized grains growth with increasing deformation temperature and decreasing strain rate.
作者
付静
孙有平
周学浩
李旺珍
王文熙
FU Jing SUN Youping ZHOU Xuehao LI Wangzhen WANG Wenxi(College of Mechanical Engineering,Guangxi University of Science and Technology, Liuzhou 545006,China)
出处
《铸造技术》
CAS
北大核心
2017年第3期513-516,共4页
Foundry Technology
基金
国家自然科学基金资助项目(51301044)
广西自然科学基金资助项目(2014GXNSFBA118246)
广西科技大学研究生教育创新计划资助项目(GKYC201604)