冷轧5083铝合金板材搅拌摩擦焊接头组织与力学性能 被引量:1

Research on the microstructure and mechanical properties of friction stir welded joints of 5083 aluminum alloy cold rolled sheet
下载PDF
导出
摘要 采用搅拌摩擦焊方法对5083铝合金进行焊接,利用维氏硬度测试机、拉伸试验机、光学显微镜和扫描电镜设备,研究了焊接工艺参数对搅拌摩擦焊接头显微组织与力学性能的影响。结果表明:焊接后的焊核区组织为等轴晶,并得到了细化;当焊接速度为100mm/min,旋转速度分别为1 200 r/min和2 000 r/min时,搅拌摩擦焊接头的抗拉强度最高为270 MPa;当焊接速度不变,旋转速度为2 000 r/min时,其伸长率最大为16.7%,焊接接头的硬度最高点均出现在焊核区。断口分析表明:断裂为韧性断裂和脆性断裂共存。 The 5083 aluminum alloy plates were welded by friction stir welding( FSW) method, and the effect of welding parameters on microstructure and mechanical properties of FSW joints were studied by means of Vickers hardness tester, tensile testing machine, optical microscope and scanning electron microscope. The results showed that microstructure of the nugget zone was fine equiaxial grain. When the welding speed of 100 mm/min, rotating speed of 1 200 r/min and 2 000 r/min, the highest tensile strength joints of FSW was 270 MPa. And with the welding speed of 100 mm/min, the rotating speed of 2 000 r/min, the maximum elongation of 16.7%, the highest value in the welded joints hardness existed in the weld nugget zone. The fractograph analysis indicated that fracture mode was ductile and brittle.
出处 《焊接技术》 2017年第2期5-8,共4页 Welding Technology
基金 国家自然科学基金资助项目(51301044)
关键词 5083铝合金 FSW 显微组织 力学性能 5083 aluminum alloy FSW microstructure mechanical properties
  • 相关文献

参考文献16

二级参考文献170

共引文献478

同被引文献7

引证文献1

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部