搅拌工艺对SiCp/A356复合材料中SiC颗粒分布及性能的影响 被引量:3

Effect of Stirring Process on SiC Particle Distribution and Properties of SiCp/A356 Composite
下载PDF
导出
摘要 采用不同的半固态搅拌工艺(变化搅拌速度和搅拌时间),制备了SiC颗粒增强A356复合材料。利用金相显微镜(OM)、扫描电镜(SEM)和磨损试验机研究了搅拌工艺参数对复合材料中SiC颗粒的分布、孔隙率以及磨损量的影响。结果表明,在搅拌速度550 r/min、搅拌时间30 min下,制备的SiCp/A356复合材料SiC颗粒分布均匀,孔隙率相对较低,耐磨性好。 SiC particle reinforced A356 composite material was prepared by semi-solid stirring at different speeds for different times. The effects of stirring parameters on the distribution of SiC particles, porosity and wear loss in the composite were investigated using metallographic microscope(OM), scanning electron microscopy (SEM) and wear testing machine. The results showed that the SiCp/A356 composite which was prepared at the mixing speed of 550 r/min and mixing time of 30 min possessed a uniform distribution of SiC particles, relatively low porosity and good wear resistance.
出处 《上海金属》 CAS 北大核心 2017年第2期5-9,共5页 Shanghai Metals
基金 "上海大学金属材料工程卓越工程师"项目的资助
关键词 SiCp/A356复合材料 SIC颗粒 半固态搅拌 搅拌速度 搅拌时间 SiCp/A356 composite, SiC particle,semi-solid stirring, stirring speed, stirring time
  • 相关文献

参考文献8

二级参考文献71

共引文献129

同被引文献39

引证文献3

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部