乙烯基酯复合材料/橡胶界面性能研究 被引量:1

Interfacial Properties of Vinyl Resin Composites and Rubber
原文传递
导出
摘要 通过对橡胶表面进行处理并涂刷柔性过渡层,研究橡胶与乙烯基树脂复合材料的界面粘接性能。结果表明,橡胶表面经过化学处理后,出现大量细小微裂纹,使得橡胶与乙烯基酯复合材料的界面粘接强度得到大幅度提高;在经过化学处理后的橡胶表面涂刷柔性能渡层,二者界面剥离强度提高到2.90 k N/m,粘合强度达到2.30 MPa。 The surface of rubber was modified and coated by connection layer and the interfacial binding of vinyl resin composite and rubber was investigated. Results showed that when the rubber surface was treated with chemical reagent,microcracks appeared on the surface,which was beneficial for the binding; when the rubber surface was chemical treated and coated with flexible connection layer,the peel strength of the interface was improved to 2. 90 k N/m and the adhesive strength 2. 30 MPa.
出处 《材料开发与应用》 CAS 2017年第2期29-33,共5页 Development and Application of Materials
关键词 乙烯基复合材料 橡胶 界面性能 vinyl resin composites rubber interfacial properties
  • 相关文献

参考文献2

二级参考文献44

  • 1陈经盛.橡胶制品防老化涂层的研究与应用[J].合成橡胶工业,1993,16(3):161-164. 被引量:7
  • 2姚芝茂,杨久义.橡胶抗臭氧老化的物理防护[J].河北化工,1996,19(2):37-39. 被引量:4
  • 3丁立朋,王仲平,马兴法,吴崇光.冷粘制鞋用处理剂[J].橡胶工业,1996,43(8):475-477. 被引量:1
  • 4刘廷信.表面处理剂在制鞋工业中的应用[J].粘接,1996,17(5):23-25. 被引量:3
  • 5Anon.Low surface energy surbstrates present bonding challenges[J].Adhesives Age,1996,39(11):38-44.
  • 6Roymond F W.Surface preparation techniques for adhesive bonding[M].New Jersey:Noyes Publications,1989:127.
  • 7Christine A,Volker S,Robert H J J.Process for hydrophilicizing the surface of polymeric substrates with a macroinitiator as primer[P].USA:USP 6 096 369,2000-08-01.
  • 8Rose A R.Coating adhesion to low surface free energy substrates[J].Progress in Organic Coating,1994,25(1):73-83.
  • 9María D Romero-Sánchez,José Miguel Martín-Martínez.Surface modification of vulcanized SBR rubber by treatment with atmospheric plasma torch[J].International Journal of Adhesion and Adhesives,2006,26(5):345-354.
  • 10María D Romero-Sánchez,M Mercedes Pastor-Blas,José Miguel Martín-Martínez.Treatment of a SBS rubber with corona discharge to improve the adhesion to polyurethane adhesive[J].International Journal of Adhesion and Adhesives,2003,23(1):49-57.

共引文献5

同被引文献15

引证文献1

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部