Alkaline zinc manganese dioxide（Zn–MnO2）batteries are widely used in everyday life. Recycling of waste alkaline Zn–MnO2 batteries has always been a hot environmental concern. In this study, a simple and costeffective process for synthesizing Mn3O4/carbon nanotube（CNT） nanocomposites from recycled alkaline Zn–MnO2 batteries is presented. Manganese oxide was recovered from spent Zn–MnO2 battery cathodes. The Mn3O4/CNT nanocomposites were produced by ball milling the recovered manganese oxide in a commercial multi-wall carbon nanotubes（MWCNTs） solution. Scanning electron microscopy（SEM） analysis demonstrates that the nanocomposite has a unique three-dimensional（3D） bird nest structure. Mn3O4 nanoparticles are homogeneously distributed on MWCNT framework. Mn3O4/CNT nanocomposites were evaluated as an anode material for lithium-ion batteries, exhibiting a highly reversible specific capacitance of -580 mA h·g^-1 after 100 cycles. Moreover, Mn3O4/CNT nanocomposite also shows a fairly positive onset potential of -0.15 V and quite high oxygen reducibility when considered as an electrocatalyst for oxygen reduction reaction.
Alkaline zinc manganese dioxide（Zn–MnO2）batteries are widely used in everyday life. Recycling of waste alkaline Zn–MnO2 batteries has always been a hot environmental concern. In this study, a simple and costeffective process for synthesizing Mn3O4/carbon nanotube（CNT） nanocomposites from recycled alkaline Zn–MnO2 batteries is presented. Manganese oxide was recovered from spent Zn–MnO2 battery cathodes. The Mn3O4/CNT nanocomposites were produced by ball milling the recovered manganese oxide in a commercial multi-wall carbon nanotubes（MWCNTs） solution. Scanning electron microscopy（SEM） analysis demonstrates that the nanocomposite has a unique three-dimensional（3D） bird nest structure. Mn3O4 nanoparticles are homogeneously distributed on MWCNT framework. Mn3O4/CNT nanocomposites were evaluated as an anode material for lithium-ion batteries, exhibiting a highly reversible specific capacitance of -580 mA h·g^-1 after 100 cycles. Moreover, Mn3O4/CNT nanocomposite also shows a fairly positive onset potential of -0.15 V and quite high oxygen reducibility when considered as an electrocatalyst for oxygen reduction reaction.
基金
financially supported by the National Natural Science Foundation of China(Nos.21671096 and 21603094)
the Shenzhen Peacock Plan(No.KQCX2014052215 0815065)
the Natural Science Foundation of Shenzhen(Nos.JCYJ20150630145302231 and JCYJ20150331101823677)
the Science and Technology Innovation Foundation for the Undergraduates of South University of Science and Technology of China(Nos.2016S10,2016S20,2015x19 and 2015x12)