空气层匹配碳纤维吸波涂层的吸波性能 被引量:3

Absorbing Properties of Carbon Fiber Absorbing Coating Matched with Air Layer
下载PDF
导出
摘要 目的探究空气层匹配厚度及碳纤维含量、长度对碳纤维吸波涂层吸波性能的影响。方法以短切碳纤维为吸收剂,水性聚氨酯为基体树脂,制备雷达吸波涂层。采用扫描电子显微镜和金相显微镜对短切碳纤维和涂层的微观形貌进行分析表征,将碳纤维涂层与空气层进行匹配,并采用矢量网络分析仪测试分析涂层的吸波性能。结果当空气匹配层厚度由1 mm逐渐增加到3.5 mm时,复合涂层的最大吸收峰由高频逐渐向低频移动。匹配厚度为3 mm时,反射率峰值最低(-41 d B)。匹配厚度为2.5 mm时,有效吸收频段(反射率<-10 d B)最宽,为8.6~18 GHz。随着碳纤维含量的增加,涂层的最大吸收峰频率均呈下降趋势,有效吸收频段向低频移动。碳纤维含量(质量分数)低于0.1%时,只有碳纤维长度达到3 mm,涂层才具备有效吸波性能。碳纤维含量为0.1%~0.2%,碳纤维长度为2 mm时,涂层吸波性能最好。碳纤维含量超出0.2%,碳纤维长度为1 mm时,涂层已经具备较好的吸波性能。结论通过调节空气层匹配厚度及碳纤维含量、长度,空气层匹配碳纤维吸波涂层在不同频段均能实现对电磁波的有效吸收。 The work aims to explore the effects of matching thickness as well as content and length of carbon fiber on ab- sorbing properties of carbon fiber absorbing coating. The radar absorbing coating was prepared with chopped carbon fiber as absorbent and waterborne polyurethane as matrix resin. Morphology of the chopped carbon fiber and the coating was analyzed and characterized by using scanning electron microscope (SEM) and metallurgical microscope. Carbon fiber coating was matched with air layer, and absorbing properties of the coating were tested by using vector network analyzer. As thickness of the air matching layer increased from 1 mm to 3.5 ram, the maximum absorption peak moved from high frequency to low frequen- cy. As the matching thickness was 3 nun, reflectivity peak was the lowest (-41 dB). As the thickness was 2.5 mm, the effective absorption frequency (〈-10 dB) was the widest (8.6 ~ 18 GHz). Maximum absorption peak frequency of the coating showed a decreasing trend as the carbon fiber content increased. When the carbon fiber content was lower than 0.1wt.%, the coating exhi-bited effective absorbing properties only when the carbon fiber length reached 3 mm. When the carbon fiber content was 0.1wt.% - 0.2wt.%, the absorbing property was the best when the carbon fiber length was 2 mm. When the carbon fiber content was over 0.2wt.%, the coating had better absorbing properties when the carbon fiber length was 1 mm. Effective absorbing properties of carbon fiber absorbing coating matched with air layer to electromagnetic wave can be achieved in several frequen- cy bands by adjusting matching thickness of air layer as well as content and length of carbon fiber.
出处 《表面技术》 EI CAS CSCD 北大核心 2017年第10期201-206,共6页 Surface Technology
基金 全军后勤科研计划项目(BY115C007) 重庆市自然科学基金(cstc2014jcyj A50026)~~
关键词 短切碳纤维 吸波涂层 匹配厚度 碳纤维含量 碳纤维长度 吸波性能 chopped carbon fiber absorbing coating matching thickness carbon fiber content carbon fiber length ab-sorbing properties
  • 相关文献

参考文献10

二级参考文献130

共引文献115

同被引文献24

引证文献3

二级引证文献6

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部