连续热镀锌带钢表面缺陷原因分析及解决措施 被引量:8

Analysis on Causes Leading to Defects on the Surface of Continuous Hot-dip Galvanizing Steel Strips and Countermeasures for the Defects
下载PDF
导出
摘要 介绍了连续热镀锌带钢镀层表面存在的各类常见缺陷,包括锌渣、气刀条痕、划伤、热褶皱、光整羽痕和压印等,并分析了缺陷产生的原因,针对缺陷提出了解决措施。实践表明,热镀锌带钢的表面质量明显改善,O5板合格率达到了90%以上。 Various kinds of common defects on the surface of continuous hot-dip galvanizing steel strips including zinc slag, steaks caused by air knife, scratches, wrinkles in hot condition,pinnate marks due to the finishing process and impressions were introduced while the causes leading to the defects were analyzed. Then countermeasures for dealing with the defects were proposed. The production practice showed that the surface quality of the hot-dip galvanizing steel strips was obviously improved and the qualified rate of O5 steel sheets was over 90%.
作者 刘超
出处 《鞍钢技术》 CAS 2017年第6期62-65,共4页 Angang Technology
关键词 连续热镀锌 表面缺陷 产生原因 控制措施 continuous hot-dip galvanizing surface defects causes controlling counter-measures
  • 相关文献

参考文献1

二级参考文献16

共引文献16

同被引文献45

引证文献8

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部