在多孔β-Ca_3(PO_4)_2(β-TCP)表面沉积含有淫羊藿苷(ICA)的丝蛋白(SF)层,制备可缓释ICA的SFICA/β-TCP骨修复复合材料,研究SF-ICA/β-TCP复合材料的相关性能。结果表明,SF-ICA/β-TCP复合材料中ICA的引入并未改变基体材料的微观形貌与孔隙率;体外释放实验表明,通过负载量的调控,可以实现SF-ICA/β-TCP复合材料中ICA的高浓度释放(2.80×10^(-4) mg/mL至7.00×10^(-4) mg/mL)和低浓度释放(5×10^(-6) mg/mL至1.0×10^(-5) mg/mL),累计释放量分别达到约5.2×10^(-3) mg和7.0×10^(-5) mg;细胞增殖实验与电镜观察表明,SF-ICA/β-TCP复合材料中ICA的负载对小鼠颅顶前骨细胞的增殖无显著性影响;但碱性磷酸酶活性检测实验表明,负载高含量ICA的SF-ICA/β-TCP复合材料中的细胞具有较高的碱性磷酸酶表达。所制备的负载ICA的SFICA/β-TCP复合材料在体内骨修复领域具有潜在的应用前景。
Using silk fibroin （SF）as a co-absorbed carrier to load the icariin （ICA）on the interface of porousβ-tricalcium phosphate （β-TCP）,the SF-ICA/β-TCP composites were abtained.The microstructure and porosity of the SF-ICA/β-TCP composite were maintained.The release tests show that the ICA release in composite can be controlled by loading amount.High release （2.80 ＆#215; 10-4 mg/mL to 7.00 ＆#215; 10-4 mg/mL）or low release （5 ＆#215; 10-6 mg/mL to 1.0＆#215;10-5 mg/mL）of the ICA has been detected and the cumulative release is 5.2＆#215;10-3 mg or 7.0＆#215;10-5 mg,respectively.The cell proliferation have and scanning electron microscopy observation has displayed no indicated significant difference between the ICA loaded or blank SF/β-TCP composite.However,there is high expression of alkaline phosphatase activity in the ICA loaded SF/β-TCP composite.The high ICA loadedβ-tricalci-um phosphate may have a potential application in bone repair in vivo.
出处
《复合材料学报》
EI
CAS
CSCD
北大核心
2017年第11期2580-2585,共6页
Acta Materiae Compositae Sinica
基金
广东省自然科学基金(2015A030310345)
广东省医学科学技术研究基金(A2015352)
广东省中医药局科研项目(20161180)
广东省科技计划(2013B010402019)
广州市属高校科研项目(1201630251)