一种新型微裂纹镀铬工艺及镀层性能研究 被引量:8

Study on A New Type of Micro-crack Chrome Plating Process and the Coating Performance
下载PDF
导出
摘要 本文研究了电镀微裂纹硬铬的工艺参数和添加剂对镀层裂纹长度、深度和密度的影响。借助3D显微镜以及SEM观察镀层表面微裂纹,并将自行研发的ND-331微裂纹镀铬工艺与标准镀铬工艺、国外知名品牌的HCR镀铬工艺进行了对比。结果表明,研发的ND-331微裂纹镀铬工艺电流效率可达20.5%,镀铬层裂纹密度为1020条/cm、硬度为989.9 HV,其性能优于标准镀铬,与HCR镀铬相当。 In this paper, the process parameters of micro- crack hard chrome plating and the effects of ad- ditives on the length, depth and density of the coating cracks were studied. The self-developed ND- 331microcrack chrome plating process was compared to the standard chrome plating process and the well- known foreign brand HCR chrome plating process by observing the surface micro-cracks with 3D micro- scope and SEM. Results showed that the current efficiency of ND-331 process was up to 20.5%, the crack density of the chrome plated coating was 1020/cm, and the hardness was 989.9 HV, its perform- ance was better than that of the standard chrome plating and equal to the HCR chrome plating.
出处 《电镀与精饰》 CAS 北大核心 2018年第1期17-21,共5页 Plating & Finishing
关键词 微裂纹铬 硬铬 镀铬添加剂 micro- crack chrome hard chrome chrome plating additive
  • 相关文献

参考文献9

二级参考文献52

共引文献72

同被引文献77

引证文献8

二级引证文献18

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部