摘要
陶瓷涂层以其优异的耐磨损、耐高温、耐腐蚀等性能表现出巨大的工程应用前景。但是,在服役过程中因温度变化和受力诱发的裂纹产生、扩展,甚至导致涂层开裂、剥落及失效,这些因素限制了涂层的应用,因此通过结构优化改善陶瓷涂层的抗开裂、剥落性能较为重要。本文首先论述了纳米结构涂层、耐磨多层涂层、复合涂层的失效机理及其结构优化。提出了利用单次喷涂制备粘结层和陶瓷层的方法,通过该方法可以消除陶瓷层与粘结层间的界面形态,提高涂层的断裂韧性、粘结强度。最后展望了陶瓷涂层在材料组分设计和工艺优化研究中应重点关注的方面。
Due to the excellent wear resistance, corrosion resistance as well as chemical stability at high temperature, the ceramic coating is widely applied in engineering setors. How- ever, due to coating cracking, expansion, peeling and failure caused by temperature and stress change during the service process, the application of the ceramic coating is restricted. It is important to improve the anti-cracking and anti-peeling performance of the ceramic coatings through structural optimization. In this paper, the failure mechanism and structure optimization of the nano-structure coating, wear-resistant multi-layer coatings and composite coatings are discussed. The one-stop spraying method for preparation of the ceramic and adhesive coating is proposed, which can eliminate the interface defects and improve fracture toughness and ad- hesion. Finally, it focus on the structure design and optimization of ceramic coating.
出处
《涂料工业》
CAS
CSCD
北大核心
2018年第3期82-87,共6页
Paint & Coatings Industry
关键词
陶瓷涂层
结构优化
复合涂层
多层涂层
失效机理
纳米涂层
ceramic coating
structure optimization
composite coating
muhilayer coat-ing
failure mechanism
nanostructure coating