摘要
针对目前有机植筋胶易老化、凝结时间长等问题,开发出一种新型碱矿渣无机植筋胶,并分析其植筋机理。通过无机胶凝材料试块的凝结时间和抗压强度试验,确定无机植筋胶的最优配合比。通过采用此无机植筋胶在混凝土基材上进行植筋拉拔试验,观察植筋试件破坏模式,研究其黏结锚固性能,并与环氧树脂有机植筋胶的黏结锚固性能进行对比。试验结果表明:该碱矿渣无机植筋胶高强快凝、黏结锚固性能及耐久性良好。
In view of the problems of organic planting glue such as easy aging and long agglomeration time,the paper developed a new kind of alkali-activated inorganic planting glue and analyzed its planting mechanism. The optimal mixing ratio of inorganic anchorage glue was determined by the experiment of setting time and compressive strength.Through the pull-out test for planting bar on the concrete substrate with inorganic glue,the bond and anchor performance of inorganic planting specimen were studied by observing the failure modes of the specimers and comparing with the bond and anchor performance of the specimens with epoxy resin organic planting glue. The results showed that the alkali-activated inorganic planting glue had high strength and fast setting,the bond and anchoring performance,and its durability was good.
作者
尚守平
杨甜
黄新中
SHANG Shouping;YANG Tian;HUANG Xinzhong(College of Civil Engineering, Hunan University, Changsha 410082, China)
出处
《工业建筑》
CSCD
北大核心
2018年第4期177-181,共5页
Industrial Construction
基金
国家“十二五”科技支撑计划项目(2015BAL03B01)
关键词
无机植筋胶
黏结锚固性能
植筋拉拔试验
破坏模式
inorganic planting glue
bond and anchor performance
pull-out test for planting bar
failure mode