Synthesis of Mg-based composite material with in-situ formed LaH_3 and its hydrogen storage characteristics 被引量:6

Synthesis of Mg-based composite material with in-situ formed LaH_3 and its hydrogen storage characteristics
原文传递
导出
摘要 In this work,a Mg-based composite material with in-situ formed LaH3, Mg2 NiH4-LiBH4 + 20 wt% LaH3,was prepared by ball milling LiBH4 and hydrogenated LaMg2 Ni and Mg2 Ni powder mixture, followed by heat treatment at 573 K. The onset dehydrogenation temperature of the composite is reduced by 50 K compared with that of Mg2 NiH4-LiBH4. The LaH3-doped composite shows faster kinetics,absorbing1.43 wt% hydrogen within 100 s at 423 K,which is 6.5 times faster than Mg2 NiH4-LiBH4. Moreover,the composite releases 1.24 wt% hydrogen within 500 s at 573 K,0.69 wt% higher than Mg2 NiH4-LiBH4. The activation energy of the composite is reduced by 8.2 and 80 kJ/mol compared with that of Mg2 NiH4-LiBH4 and commercial MgH2, respectively. The improvement in hydrogen storage properties is attributed to the fact that LaH3 promotes the generation of nano-sized spongy Mg structure, which has good catalytic activity during the subsequent hydrogenation/dehydrogenation process. In this work,a Mg-based composite material with in-situ formed LaH3, Mg2 NiH4-LiBH4 + 20 wt% LaH3,was prepared by ball milling LiBH4 and hydrogenated LaMg2 Ni and Mg2 Ni powder mixture, followed by heat treatment at 573 K. The onset dehydrogenation temperature of the composite is reduced by 50 K compared with that of Mg2 NiH4-LiBH4. The LaH3-doped composite shows faster kinetics,absorbing1.43 wt% hydrogen within 100 s at 423 K,which is 6.5 times faster than Mg2 NiH4-LiBH4. Moreover,the composite releases 1.24 wt% hydrogen within 500 s at 573 K,0.69 wt% higher than Mg2 NiH4-LiBH4. The activation energy of the composite is reduced by 8.2 and 80 kJ/mol compared with that of Mg2 NiH4-LiBH4 and commercial MgH2, respectively. The improvement in hydrogen storage properties is attributed to the fact that LaH3 promotes the generation of nano-sized spongy Mg structure, which has good catalytic activity during the subsequent hydrogenation/dehydrogenation process.
出处 《Journal of Rare Earths》 SCIE EI CAS CSCD 2018年第7期739-744,共6页 稀土学报(英文版)
基金 supported by the National Natural Science Foundation of China(51771164,51571173) China Postdoctoral Science Foundation(2016M601281) Scientific Research Projects in Colleges and Universities in Hebei Province,China(ZD2014004,QN2016002)
关键词 MG2NIH4 LiBH4 Composite Hydrogen storage properties Lanthanum hydride Rare earths Mg2NiH4 LiBH4 Composite Hydrogen storage properties Lanthanum hydride Rare earths
  • 相关文献

参考文献2

二级参考文献19

  • 1Lu J, Choi Y J, Fang Z Z, Sohn H Y, Ronnebro E. Hydro?gen storage properties of nanosized MgH2-0.1 TiH2 pre?pared by ultrahigh-energy-high-pressure milling. J. Am. Chem. Soc., 2009,131: 15843.
  • 2Anik M, Karanfil F, Kucukdeveci N. Development of the high performance magnesium based hydrogen storage al?loy. Int. J. Hydrogen Energy, 2012, 37: 299.
  • 3Zhong H C, Wang H, Ouyang L Z, Zhu M. Microstructure and hydrogen storage properties of Mg-Sn nanocomposite by mechanical milling. J. Alloys Compd., 2011, 509: 4268.
  • 4Li X, Zhao D L, Zhang Y H, Xu J Y, Zhang G F, Zhang Y. Hydrogen storage properties of mechanically milled La2Mgn-x wt.%Ni (=0, 50, 100, 150 and 200) compos?ites. J. Rare Earths, 2013, 31: 694.
  • 5Zhang Y H, Hu F, Li Z, Lil K, Guo S, Wang X L. Hydro?gen storage characteristics of nanocrystalline and amor?phous Mg-Ni-type alloys prepared by melt spinning. J. Alloys Compd., 2011, 509: 294.
  • 6Lin H J, Ouyang L Z, Wang H, Liu J W, Zhu M. Phase transition and hydrogen storage properties of melt-spun Mg3LaNiO.l alloy. Int. J. Hydrogen Energy, 2012, 37: 1145.
  • 7Poletaev A A, Denys R V, Solberg J K, Tarasov B P, Yar?tys V A. Microstructural optimization ofLaMg12 alloy for hydrogen storage. J. Alloys Compd., 2011, 509S: S633.
  • 8Zheng Q, Pivak Y, Mooij L P A, Van der Eerden A M J, Schreuders H, Jongh de P E, Bitter J H, Dam B. EXAFS investigation of the destabilization of the Mg-Ni- Ti (H) system. Int. J. Hydrogen Energy, 2012, 37: 4161.
  • 9Liu T, Zhang T W, Qin C G, Zhu M, Li X G. Improved hydrogen storage properties of Mg-V nanoparticles pre?pared by hydrogen plasma-metal reaction. J. Power Sources, 2011,196: 9599.
  • 10Loken S, Solberg J K, Maehlen J P, Denys R V, Lototsky M V, Tarasov B P, Yartys V A. Nanostructured Mg-Mm?Ni hydrogen storage alloy: Structure-properties relation?ship. J. Alloys Compd., 2007, 446-447: 114.

共引文献18

同被引文献23

引证文献6

二级引证文献22

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部