隆起缺陷使带钢产生附加浪形,造成产品降级。为加强对隆起缺陷的认识及控制,首先对隆起缺陷进行了分类,然后分析了不同缺陷的特征及形成原因,并根据产生的不同原因提出了相应的控制措施。
The uplift defect causes the strip wave,and degrades the strip quality.In order to strengthen the cognition and control of this defects,the defects were classified,then its characteristics and the causes were analyzed.Some corresponding measures were proposed with good effect.