180 t RH真空精炼炉脱硫工艺开发及应用 被引量:5

Development and application of desulfurization process for 180 t RH vacuum refining furnace
原文传递
导出
摘要 针对铝镇静无取向硅钢成品硫质量分数超标问题,开发了RH脱硫工艺。通过选择合适的脱硫渣系以及工艺参数,使RH工位脱硫率达到30%~60%,W800系列无取向硅钢成品w([S])≤0.005 0%,达标率由72.19%提高至98%以上,同时确保了RH出钢w(T[O])〈0.002 0%,w([N])〈0.001 5%。通过转炉出钢和RH过程炉渣脱氧改质,将RH出钢渣中w((TFe))控制在3%以下,RH过程炉渣碱度保持在5.0以上,使渣-钢之间硫的分配比达到80~260,有助于提高RH脱硫效果。 The desulfurization technology in the RH process was developed to reducethe sulfur mass percent in the nonoriented silicon steel. The desulfurization degree was controlled at 30%-60% in a RH reactor,and the ratio of in the W800 non-oriented silicon steel with w([S])≤ 0.005 0% was increased from 72.19% upto 98%. Meanwhile,this process was able to ensure that w(T[O])〈 0.002 0% and w([N])〈 0.001 5% at the end of the RH treatment. Through the slag deoxy-modification during the tapping and the RH treatment,w((TFe)) at the end of the RH treatment was controlled below 3%. The slag basicity was kept above 5.0,and the sulfur distribution ratio between slag and steel was controlled at 80-260,which is favored to the improvement of the desulfurization process in the RH treatment.
作者 赵家七 蔡小锋 邹长东 ZHAO Jia-qi;CAI Xiao-feng;ZOU Chang-dong(Institute of Research of Iron and Steel,Jiangsu Province(Shasteel),Zhan~iagang 215625,Jiangsu,China)
出处 《钢铁》 CAS CSCD 北大核心 2018年第11期41-46,共6页 Iron and Steel
关键词 无取向硅钢 RH真空炉 脱硫剂 钢包渣 non-oriented silicon steel RH vacuum furnace desulfurizer ladle slag
  • 相关文献

参考文献10

二级参考文献72

共引文献170

同被引文献116

引证文献5

二级引证文献20

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部