Phase Analysis of Cemented Carbide WC-Co Boronised with Yttrium

Phase Analysis of Cemented Carbide WC-Co Boronised with Yttrium
下载PDF
导出
摘要 Phase analysis for the coated surface with B 4C and Y 2O 3 of cemented carbide WC-20Co in vacuum-heating was carried out by high-temperature X-ray diffraction from ambient temperature to 1300 ℃. The results show that, the high-concentration active boron atoms are released from the boron-supply agent B 4C located on the alloy surface and diffused into the γ-phase, leading to forming the three-element boron-bearing compound W 2Co 21B 6 beside forming boron-bearing compounds on the blank surface. By contrast with boronising only, the element yttrium in boronization broadens the boronising temperature range during vacuum-sintering, catalyzes the decarbonisation decomposition of B 4C and promotes diffusion of active boron atoms into the bulk of WC-Co. Phase analysis for the coated surface with B 4C and Y 2O 3 of cemented carbide WC-20Co in vacuum-heating was carried out by high-temperature X-ray diffraction from ambient temperature to 1300 ℃. The results show that, the high-concentration active boron atoms are released from the boron-supply agent B 4C located on the alloy surface and diffused into the γ-phase, leading to forming the three-element boron-bearing compound W 2Co 21B 6 beside forming boron-bearing compounds on the blank surface. By contrast with boronising only, the element yttrium in boronization broadens the boronising temperature range during vacuum-sintering, catalyzes the decarbonisation decomposition of B 4C and promotes diffusion of active boron atoms into the bulk of WC-Co.
出处 《Journal of Rare Earths》 SCIE EI CAS CSCD 2002年第4期287-290,共4页 稀土学报(英文版)
基金 ProjectsupportedbytheNaturalScienceFoundationofTianjin( 9936 0 2 811)
关键词 rare earths cemented carbide WC-Co vacuum-sintering rare earth-boronization rare earths cemented carbide WC-Co vacuum-sintering rare earth-boronization
  • 相关文献

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部