摘要
Poly(aspartic acid-itaconic acid) copolymer was synthesized from aspartic acid(Asp) and itaconic acid(Ita) under microwave irradiation. The effects of microwave power, microwave irradiation time, molar ratio of itaconic acid and aspartic acid, catalyst type, catalyst and organic solvent content on copolymer yield, and the performance for inhibition of CaCO_3 fouling were investigated. It was found that the product yield achieved a highest record of 95% when the amount of catalyst Na H_2PO_4 was 0.012 mol, the amount of organic solvent propylene carbonate was 16 m L, the molar ratio of Asp/Ita was 3:1, the microwave output power was 1200 W and the irradiation time was 5.5 min. And the product performance for inhibition of calcium carbonate also reached a highest value of 94.38%. Structural characterization of the product showed that the product was the aspartic acid-itaconic acid copolymer.
Poly(aspartic acid-itaconic acid) copolymer was synthesized from aspartic acid(Asp) and itaconic acid(Ita) under microwave irradiation. The effects of microwave power, microwave irradiation time, molar ratio of itaconic acid and aspartic acid, catalyst type, catalyst and organic solvent content on copolymer yield, and the performance for inhibition of CaCO_3 fouling were investigated. It was found that the product yield achieved a highest record of 95% when the amount of catalyst Na H_2PO_4 was 0.012 mol, the amount of organic solvent propylene carbonate was 16 m L, the molar ratio of Asp/Ita was 3:1, the microwave output power was 1200 W and the irradiation time was 5.5 min. And the product performance for inhibition of calcium carbonate also reached a highest value of 94.38%. Structural characterization of the product showed that the product was the aspartic acid-itaconic acid copolymer.
基金
supported financially from the National Natural Science Foundation of China (Grant No. 51308211)
the State Key Laboratory of Urban Water Resource and Environment (HIT) (Grant No. ES200903)
the Fundamental Research Funds for the Central Universities (Grant No. 2015MS63)