真空感应炉冶炼铁铬铝合金铸锭常见缺陷成因分析及改善措施 被引量:2

Cause analysis and improvement measures of common defects in Fe-Cr-Al alloy ingots smelted by VIM furnace
原文传递
导出
摘要 实验研究了150kg真空感应炉冶炼铁铬铝合金铸锭常见缺陷成因分析及改善措施。本文设计了4种不同的实验方案,研究了浇注温度、浇注时间、炉衬使用次数和中间包是否使用过滤器对钢锭表面质量及内部缩孔的影响情况。结果表明,浇注温度为1640℃、浇注时间为0.56 min、中间包使用过滤器、炉衬使用次数越少的条件下钢锭表面质量较好且内部无缩孔缺陷。 This paper studied the cause and the improvement measures of common defects in Fe-Cr-Al alloy ingots smelted by150 kg VIM furnace. Through four experiments, the influence of pouring temperature, pouring time, the lining use times and whether the tundish used a filter are studied on the surface quality and the internal shrinkage. The results show that the surface quality of the ingot is better and there is no shrinkage cavity defect under the condition that the pouring temperature is 1640 ℃,the pouring time is 0.56 min, the lining is used less and the tundish uses the filter.
作者 姜彩伟 刘建民 胡显军 JIANG Cai-wei;LIU Jian-min;HU Xian-jun(Institute of Research of Iron and Steel, Shasteel, Zhangjiagang 215625, China)
出处 《真空》 CAS 2019年第2期74-77,共4页 Vacuum
关键词 真空感应炉 铁铬铝合金 缺陷 措施 VIM Fe-Cr-Al alloy defect measures
  • 相关文献

参考文献1

二级参考文献12

  • 1D. Zhang and G. Dehm: Scripta Mater., 2000, 42, 1065.
  • 2J.P. Campell, K.T. Venkateswara and R.O. Ritchie: Metal1. Mater. Trans. A, 1999, 30(3), 563.
  • 3Y.Y. Chen, F.T.Kong, J.C. Han and Z.Y. Chen: Intermetallics, 2005, 13, 263.
  • 4T. Degawa, K. Kamata and Y. Nagashima: Proc. Int. Symp. on Intermetallic Compound (JIMIS-6), ed. O. Izumi, Japan Institute of Metals, 1991, 1003.
  • 5~ A T. Kawabata, T. Abumiya and O'. Izumi: Acta Metall. Mater., 1992, 40(10), 2557.
  • 6W. Lefebvre, A. Loiseau and A. Menaad: Gamma Titanium Aluminides 2003, eds. Y.W. Kim, H. Clemens and A.H. Rosenberger, TMS. 2003, 63.
  • 7C. Frueh, D.R. Poirier, M.C. Maguire and R.A. Harding: Int. J. Cast Mteals Res., 1996, 9, 133.
  • 8F.Tsukihashi, E. Tawara and T. Hatta: Metall. Mater. Trans. B, 1996, 27(12), 967.
  • 9~ r T. H. Obake, T. Oishi and K. Ono: Metall. Trans. B, 1992, 23(10), 583.
  • 10K. Sakamoto, K. Yoshikawa, T. Kusamichi and T.Onoye: ISIJ Int., 1995, 32, 616.

共引文献8

同被引文献15

引证文献2

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部