聚偏氟乙烯超疏水纳米纤维膜的制备及性能研究 被引量:8

Preparation of PVDF super-hydrophobic nanofiber membrane
原文传递
导出
摘要 以聚偏氟乙烯(PVDF)粉末为原料,将N,N-二甲基甲酰胺与丙酮按体积比8∶2配制成含量和黏度可控的纺丝液,用静电纺丝法制备了PVDF超疏水纳米纤维膜。利用扫描电子显微镜和图像分析软件对所制纳米纤维膜的形貌、孔径分布及孔隙率、表面接触角、纯水通量等进行分析,考察了纺丝液含量、施加电压、接收距离、纺丝速度对超疏水纳米纤维膜的影响。结果表明,在纺丝液含量为10%(质量分数)、施加电压为18kV、接收距离为15cm、纺丝速度为1.0mL/h条件下,通过连续静电纺丝制备的超疏水纳米纤维膜具备最优的防水效果。 Polyvinylidene fluoride(PVDF)powder was used as raw material,and N,N-dimethylformamide and acetone were prepared into a spinning solution with controlled content and viscosity at volume ratio of 8∶2.PVDF superhydrophobic nano-particles were prepared by electrospinning method.The morphology,pore size distribution,porosity,surface contact angle and pure water flux of prepared nanofiber membrane were analyzed by scanning electron microscopy and image analysis software.The content of spinning solution,the applied voltage,the receiving distance and spinning speed were investigated.The results showed that under the condition of the spinning solution content of 10%(mass fraction),the applied voltage of 18 kV,the receiving distance of 15 cm and the spinning speed of 1.0 mL/h,continuous static electricity was passed.The superhydrophobic nanofiber membrane prepared by spinning had the best waterproof effect.
作者 孙晶 王瑞 孙红玉 申妮 徐磊 Sun Jing;Wang Rui;Sun Hongyu;Shen Ni;Xu Lei(School of Textiles,Tianjin Polytechnic University,Tianjin 300387;School of Material Engineering,Tianjin Polytechnic University,Tianjin 300387;Institute of Smart Wearable Electronic Textiles,Tianjin 300387;Huafang Co.,Ltd.,Binzhou 256617)
出处 《化工新型材料》 CAS CSCD 北大核心 2019年第4期115-119,124,共6页 New Chemical Materials
基金 国家自然科学基金青年基金项目(51303131)
关键词 静电纺丝 聚偏氟乙烯纤维 纳米纤维 疏水膜 性能 electrospinning polyvinylidene fluoride fiber nanofiber hydrophobic membrane performance
  • 相关文献

参考文献4

二级参考文献37

  • 1袁晓燕,吴卫星,盛京.熔融电纺制备PE/PP共混纤维[J].天津大学学报,2006,39(10):1232-1236. 被引量:5
  • 2万玉芹,何吉欢,俞建勇,吴玥.超声波振动在静电纺丝技术中的应用[J].纳米科技,2006,3(5):55-58. 被引量:9
  • 3Jayesh Doshi, et a I. [J]. Journal of Electrostatics. 1995,35(2-3):151-160.
  • 4Formhals A. Process and apparatus for preparing artificialthreads: US 1975504[P] ,1934-10-02.
  • 5Darrell H Reneker, Alexander L Yarin. [J]. Polymer, 2008, 49(10):2387-2425.
  • 6Teo W E, Ramakrishna S. [J]. Nanotechnology,2006,17(14):89-106.
  • 7Kim G H, ChoY S, Kim W I). [J]. Eur Polym J,2006, 42(9):2031.
  • 8Petrik S,Maly M. Production Nozzle-Less ElectrospinningNanofiber Technology [C]. Boston; 2009 Fail MRS Symposi-um ,2009.
  • 9Fong H,Chun I, Reneker D H. [ J ]. Polymer, 1999,40( 16):4585-4592.
  • 10Dietmar W Hutmacher, Paul D Dalton. [J]. Chem. Asian J ,2011,6(1):44-56.

共引文献28

同被引文献59

引证文献8

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部