摘要
A Cu/Al galvanic couple was established to study the influence of the oxidantKMnO_4 on the film-forming process of rare earth metal (REM) conversion coating on LY12 aluminumalloy. It is found that the galvanic couple simulative experiment accords with the actual immersion,and it can be substantially used to simulate the behavior of LY12 aluminum alloy in thefilm-forming process. It is showed that the formation of the coating is quickened in CeCl_3 solutioncontaining KMnO_4 compared with that not containing KMnO_4. XPS results reveal that the coatingformed on cathode is composed of oxide or hydroxide of Ce and Mn, so the mechanism of formation ofREM conversion coating changes when KMnO4 is added.
A Cu/Al galvanic couple was established to study the influence of the oxidantKMnO_4 on the film-forming process of rare earth metal (REM) conversion coating on LY12 aluminumalloy. It is found that the galvanic couple simulative experiment accords with the actual immersion,and it can be substantially used to simulate the behavior of LY12 aluminum alloy in thefilm-forming process. It is showed that the formation of the coating is quickened in CeCl_3 solutioncontaining KMnO_4 compared with that not containing KMnO_4. XPS results reveal that the coatingformed on cathode is composed of oxide or hydroxide of Ce and Mn, so the mechanism of formation ofREM conversion coating changes when KMnO4 is added.
基金
[This work was financially supported by the National Natural Science Fund of China (No.59771067).]