铁路货车车厢焊接修复时焊缝开裂分析 被引量:2

Analysis on cracks occurred in welding repair of railway freight cars
下载PDF
导出
摘要 针对铁路货车车厢在焊接修复过程中存在的焊缝开裂问题进行原因分析,从焊接引弧处的脆性组织、焊接拘束应力、焊缝结构设计、焊材结构选用、焊缝金属中的扩散氢含量,近缝区母材表面的锈蚀、氧化物对焊接质量的影响等方面入手,提出了铁路货车车厢焊接修复的工艺过程与方法。对提高货车车厢修复质量有良好的指导意义。 The causes of weld cracking in the welding repair process of railway freight cars are analyzed.The brittle structure,welding restraint stress,weld structure design,welding material structure selection,and diffusion hydrogen content in the weld metal are obtained from the welding arc.The corrosion of the surface of the base material in the near seam area and the influence of oxide on the welding quality were analyzed.The process and method of welding and repairing the railway freight car compartment were put forward.It has a good guiding significance for improving the repair quality of truck compartments.
作者 白利兵 BAI Libing(Shenmu Vocational&Technical College,Shenmu 719300,China)
出处 《电焊机》 2019年第8期104-109,共6页 Electric Welding Machine
关键词 铁路货车车厢 焊接修复 拘束应力 焊接材料 扩散氢 铁锈 railway freight cars welding repair restraint stress welding material diffusion hydrogen corrosion
  • 相关文献

参考文献3

二级参考文献5

  • 1尹士科,黄古粉,王移山.焊缝中的氢及其逸出行为[J].焊接,1987(4):6.
  • 2AMD. ISO 3690:2000 (E) Welding and Allied Processes-De- termination of Hydrogen Content in Ferritic Steel Arc Weld Metal [S]. Switzerland~ MOD,2001.
  • 3吕向阳,尹士科,张有为.高强度钢氢陷井行为的定量研究[C].第六届全国焊接学术会议论文选集.西安:中国机诫工程学会,1990:6.
  • 4王移山,尹士科.水银法测定焊缝扩散氢的影响因素[J].钢铁研究学报,2000,12(1):59-62. 被引量:6
  • 5沈胜龙.焊接技术常见缺陷的危害和防止措施[J].散文百家(下旬刊),2015,0(2):170-170. 被引量:1

共引文献17

同被引文献14

引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部