Mn掺杂对尖晶石型NiFe1.97Pd0.03O4-δ催化剂脱硝性能的影响 被引量:2

Effect of Mn-doped spinel catalyst NiFe1.97Pd0.03O4-δ on catalytic performance for SCR
下载PDF
导出
摘要 采用生物模板法,通过掺杂Mn对尖晶石型NiFe1.97Pd0.03O4-δ催化剂中的Fe离子进行取代,制备一系列不同Mn掺杂量的NiFe1.97-xMnxPd0.03O4-δ催化剂(x=0、0.01、0.02、0.05、0.10),并在单管固定床反应器中进行H2-SCR脱硝性能评价。运用X射线衍射仪(X RD)、场发射扫描电子显微镜(FE-SEM)、程序升温-脱附(N H3-TPD)和程序升温还原(H 2-TPR)以及傅里叶红外光谱仪(FTIR)等手段对催化剂进行表征、分析。结果表明:适量Mn的掺杂不仅可以提高活性物种Pd在催化剂上的分散度,还显著提高了其催化剂表面的总酸量及其氧化还原能力,从而提高了NiFe1.97Pd0.03O4-δ催化剂在低温下的H2-SCR脱硝活性,并拓宽了其催化活性温度窗口。在实验范围内,NiFe1.92Mn0.05Pd0.03O4-δ催化剂在150℃下的NO转化率高达95%,且在150~200℃温度区间内,NO转化率均在90%以上。 Spinel catalyst NiFe1.97-xMnxPd0.03O4-δwas prepared by using a biological template and then was applied for the selective catalytic reduction of NO with hydrogen(H2-SCR)in a single-tube fix-bed reactor.A series of spinel catalysts was obtained by doping Mn with different molar ratio of Mn to Ni.The catalysts were characterized by X-ray diffraction(XRD),field emission scanning electron microscope(FE-SEM),Fourier transform infrared spectroscopy(FTIR),NH3 temperature-programmed desorption(NH3-TPD)and H2 temperature-programmed reduction(H2-TPR).The results indicated that the catalysts doped with suitable amount of Mn had significantly improved the dispersion of the active specie Pd,the total acid content on the catalyst surface and the ability to oxidation,leading to enhanced de-NOx performance of NiFe1.97Pd0.03O4-δcatalyst at low temperature and a broadened active temperature window.Within the scope of the experiments,the NO conversion of NiFe1.92Mn0.05Pd0.03O4-δcatalyst was up to 95%at 150℃,and maintained above 90% at 150200℃.
作者 赵跃飞 闫涛涛 陈凯 霍超 ZHAO Yuefei;YAN Taotao;CHEN Kai;HUO Chao(Institute of Industrial Catalysis,Zhejiang University of Technology,Hangzhou 310014,Zhejiang,China)
出处 《化工进展》 EI CAS CSCD 北大核心 2020年第2期577-583,共7页 Chemical Industry and Engineering Progress
基金 浙江省自然科学基金(LY18B060015)
关键词 生物模板 尖晶石 MN掺杂 H2-SCR 催化剂 bio-templating spinel Mn-doping H2-SCR catalyst