2024铝合金粉末选区激光熔化成形工艺研究 被引量:2

Study on Selective Laser Melting Forming Process of 2024 Al Alloy Powder
原文传递
导出
摘要 采用自主研发的金属增材制造设备对2024铝合金粉末进行了选区激光熔化成形,研究了不同工艺参数下该合金的显微组织及室温拉伸性能。结果表明,激光功率为260 W,扫描速度900 mm/s,扫描间隔0.12 mm时,2024铝合金显微组织细小,结构致密,抗拉强度为372 MPa,伸长率为6.1%,具有较高的室温力学性能。 The selective laser melting of 2024 aluminum alloy powder was carried out by using the metal additive manufacturing equipment developed by ourselves. The microstructure and tensile properties of the alloy at room temperature were studied under different technological parameters. The results show that when the laser power is 260 W,the scanning speed is 900 mm/s, and the scanning interval is 0.12 mm, the 2024 aluminum alloy has fine microstructure,dense structure, tensile strength of 372 MPa, elongation of 6.1%, and high mechanical properties at room temperature.
作者 张红昌 宋彬 邢明 ZHANG Hongchang;SONG Bin;XING Ming(Beijing Hengli Technology Co.,Ltd.,Beijing 102600,China)
出处 《铸造技术》 CAS 2020年第1期22-24,共3页 Foundry Technology
关键词 选区激光熔化 2024Al合金 力学性能 selective laser melting 2024 Al alloy mechanical properties
  • 相关文献

参考文献9

二级参考文献78

共引文献138

同被引文献48

引证文献2

二级引证文献19

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部