UF树脂和MF树脂共混特性研究 被引量:2

Blend Characteristics of MF+UF Resin Mixture
下载PDF
导出
摘要 为研究脲醛树脂(UF)和三聚氰胺甲醛树脂(MF)及其共混树脂(MF+UF)的贮存特性,采用“碱-酸-碱”工艺分别合成了UF树脂和MF树脂,其摩尔比分别为1.3和2.0。将制备好的UF和MF树脂进行简单搅拌共混,得到MF+UF树脂,监测共混前后树脂及在贮存一段时间后的性能变化,如外观形态、pH值、黏度、固化时间及结构等性能。结果表明,共混后树脂的固含量介于UF和MF之间;稳定性明显提升,贮存期可达3个月,固化速度则无明显差异;核磁共振图谱(NMR)分析得出,共混树脂中的亚甲基桥键比例提高至24.13%,亚甲基醚键比例则下降至25.03%,这种结构比例的变化为共混树脂稳定性的提高提供了理论支撑。 Urea-formaldehyde(UF)resin and melamine-formaldehyde(MF)resin were synthesized by“alkaline-acid-alkaline”process with molar ratios of 1.3 and 2.0,respectively,to investigate the storage behaviors of mixed UF and MF resin.The mixture MF+UF resin was prepared by simple mechanical blending method,the performances of the resin were evaluated during the storage,such as color,pH,viscosity and curing time,and the structure.The results showed that the solid content of blended resin maintained in between the solid content of UF and MF resin;the stability increased with significantly prolonged storage life(3 months).No significant difference in curing speed was found.The proportion of methylene bridge bond in the blended resin increased to 24.13%,while the proportion of methylene ether bond decreased to 25.03%by the NMR interpretation.The structure change would provide theoretical support for longer storage time of blended MF+UF resin.
作者 周晓剑 张俊 王文丽 谢瑾 杜官本 ZHOU Xiao-jian;ZHANG Jun;WANG Wen-li;XIE Jin;DU Guan-ben(Yunnan Provincial Key Laboratory of Wood Adhesives and Glued Products,Southwest Forestry University,Kunming 650224,Yunnan,China)
机构地区 西南林业大学
出处 《西北林学院学报》 CSCD 北大核心 2020年第3期202-206,共5页 Journal of Northwest Forestry University
基金 云南省教育厅科学研究基金项目(2017ZZX209) 西南林业大学校启动基金项目(111814) 云南省中青年学术和技术带头人后备人才(2019HB026)。
关键词 三聚氰胺-尿素-甲醛树脂 脲醛树脂 三聚氰胺甲醛树脂 共混特性 melamine-urea-formaldehyde resin(MUF) urea-formaldehyde resin(UF) melamine-formaldehyde resin(MF) blend characteristics