在高温水蒸气气氛中碳化硅质耐火材料抗氧化性能研究 被引量:6

Research on oxidation resistance of silicon carbide refractories in high temperature steam
下载PDF
导出
摘要 为了改善垃圾焚烧炉内衬材料,研究了Si3N4-SiC、Si2N2O-SiC、SiAlON-SiC 3种材料在1 000℃高温水蒸气气氛下,经过50、100、150、200、250和300 h不同时间热处理后的抗氧化性能。检测了氧化前后试样的显气孔率和体积密度,计算了试样氧化前后的质量变化率和体积变化率;采用XRD和SEM分析了试样氧化前后的物相组成和显微结构。结果表明:随着氧化时间的延长,碳化硅质耐火材料的体积膨胀和质量在不断增加;Si2N2O-SiC材料明显具有较小的质量增加率和体积膨胀量;Si2N2O-SiC材料具有更好的抗氧化性能,更适合作为垃圾焚烧炉的内衬材料。 In order to improve the lining materials of waste incinerators,three kinds of refractories(Si 3N 4-SiC,Si 2N 2O-SiC,and SiAlON-SiC)were heat treated at 1000℃in steam atmosphere for 50,100,200,250,and 300 h,respectively,and the oxidation resistance was researched.The apparent porosity and the bulk density of the samples before and after oxidation,and the mass change rate and the volume expansion rate of the samples after oxidation were measured.The phase composition and the microstructure before and after oxidation were analyzed by XRD and SEM.The results indicate that with the prolongation of the oxidation time,the volume expansion and the mass of the silicon carbide refractories gradually increase;Si 2N 2O-SiC has the lower mass increase rate and volume expansion,and the better oxidation resistance,which is more suitable as the lining material for waste incinerators.
作者 相宇博 王文武 司瑶晨 曹会彦 吴吉光 万龙刚 黄志刚 王佳平 Xiang Yubo;Wang Wenwu;Si Yaochen;Cao Huiyan;Wu Jiguang;Wan Longgang;Huang Zhigang;Wang Jiaping(State Key Laboratory of Advanced Refractories,Sinosteel Luoyang Institute of Refractories Research Co.,Ltd.,Luoyang 471039,Henan,China;不详)
出处 《耐火材料》 CAS 北大核心 2020年第3期228-232,共5页 Refractories
基金 洛阳市重大科技专项(1901001A)。
关键词 碳化硅质材料 高温水蒸气 抗氧化性 物理性能 显微结构 silicon carbide refractories high temperature steam oxidation resistance physical properties microstructure
  • 相关文献

参考文献4

二级参考文献18

共引文献67

同被引文献95

引证文献6

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部