PVDF超疏水微孔膜调控研究 被引量:6

Study on the control of PVDF superhydrophobic microporous membrane
下载PDF
导出
摘要 提高疏水膜表面的疏水性是降低其应用过程中润湿风险的有效方法.为了便捷有效地调控膜结构从而提高膜的疏水性,采用非溶剂致相分离法,以水作为非溶剂添加剂,希望通过调节初生膜的预蒸发时间这一最便捷的手段,调控膜的结构及疏水性.结果表明,随着预蒸发时间的延长,铸膜液黏度增加,有利于膜表面凝胶化的形成,从而在膜表面构建出均一超疏水结构.当预蒸发时间达到120 s时,膜表面的水接触角达到151.2°,膜的气体渗透通量为40.9 mL/(m2·s·Pa),透水压力达到65.3 kPa. Improving the hydrophobicity of hydrophobic membrane surface is an effective way to reduce the wetting risk during its application.In order to control the membrane structure conveniently and effectively and improve the hydrophobicity of the membrane,H2O was added to the dope solution as non-solvent additive by non-solvent induced phase separation method.The membrane structure and hydrophobicity have been controlled by adjusting the pre-evaporation time of primary membrane.The results showed that with the increase of pre-evaporation time,the viscosity of the dope solution increased,which was conducive to the formation of gelation on the surface of the membrane,thereby creating a uniform super-hydrophobic structure on the membrane surface.When the pre-evaporation time reached 120 s,the water contact angle of the membrane was 151.2°,the gas permeation flux of the membrane was 40.9 mL/(m2·s·Pa),and the LEP was 65.3 kPa.
作者 张仁伟 刘四华 汤超 厍景国 武春瑞 吕晓龙 ZHANG Renwei;LIU Sihua;TANG Chao;SHE Jingguo;WU Chunrui;LYU Xiaolong(State Key Laboratory of Separation Membranes and Membrane Processes, School of Materials Science and Engineering, Tiangong University, Tianjin 300387, China)
出处 《膜科学与技术》 CAS CSCD 北大核心 2020年第3期7-13,21,共8页 Membrane Science and Technology
基金 国家自然科学面上基金项目(51578376)。
关键词 聚偏氟乙烯 疏水膜 非溶剂致相分离 预蒸发时间 非溶剂添加剂 polyvinylidene fluoride hydrophobic membrane non-solvent induced phase separation method pre-evaporation time non-solvent additive
  • 相关文献

参考文献1

二级参考文献7

  • 1吕晓龙,马世虎,陈燚.一种多孔分离膜孔径及其分布的测定方法[J].天津工业大学学报,2005,24(2):6-8. 被引量:7
  • 2吕晓龙.超滤膜孔径及其分布的测定方法──Ⅰ.常用测定方法讨论[J].水处理技术,1995,21(3):137-141. 被引量:28
  • 3中华人民共和国海洋行业标准.HY/T065-2002,聚偏氟乙烯微孔滤膜[S].北京:中国标准出版社,2002.
  • 4中华人民共和国海洋行业标准.HY/T112-2008,超滤膜及其组件[S].北京:中国标准出版社,2008.
  • 5中华人民共和国海洋行业标准.HY/T051-1999,中空纤维超滤膜测试方法[S].北京:中国标准出版社,1999.
  • 6中华人民共和国国家标准.GB/T20103-2006,膜分离技术术语[S].北京:中国标准出版社,2006.
  • 7ASTM Standards, F316-03, Standard Test Methods for Pore Size Characteristics of Membrane Filters by Bubble Point and Mean Flow Pore Test[S]. ASTM International, United States, 2003.

共引文献44

同被引文献34

引证文献6

二级引证文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部