Simulation on stress of large diameter CADI grinding ball based on ANSYS

下载PDF
导出
摘要 The falling ball tests were carried out on theΦ125 mm diameter Carbidic Austempered Ductile Iron(CADI)grinding balls with Mn content of 2.0wt.%,2.3wt.%,2.6wt.%and 3.0wt.%,respectively,and the kind of grinding ball with the most serious spalling was selected for stress simulation.The stress distribution between four grinding balls in the elbow of the falling ball test device when they collided with each other was simulated based on ANSYS.Results of the falling ball tests show that the spalling and mass loss of a CADI grinding ball increases with the increase of Mn content,and the CADI grinding ball with 3.0wt.%Mn shows the most obvious spalling and mass loss.The simulation results of stress distribution of a CADI grinding ball show that the maximum impact stress does not appear in the center of the contact area,but in the annular area(inner diameter of^20 mm and outer diameter of^50 mm)in the section with a depth of 5-15 mm below the grinding ball surface.The actual spalling of the ball is consistent with the simulation results,and the oxide-based impurities in CADI grinding ball accelerate the spalling of the grinding ball in service.
出处 《China Foundry》 SCIE 2020年第3期227-234,共8页 中国铸造(英文版)
基金 the Natural Science Foundation of Hebei Province of China under Grant Nos.E2016202100 and E2017202095 the National Natural Science Foundation of China(NSFC)under Grant No.51601054 the Scientific and Technological Transformative Project of Tianjin Supporting Beijing-Tianjin-Hebei under Grant No.18YFCZZC00030。
  • 相关文献

参考文献4

二级参考文献13

共引文献14

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部