耐磨钢厚度截面组织性能演变规律 被引量:6

Evolution of microstructure and properties of thickness section of wear-resistant steel
原文传递
导出
摘要 利用OLYMPUS GX71光学显微镜、场发射扫描电镜Quanta450和JEM2100F型透射电镜等手段对60 mm厚淬火态以及淬火+回火态耐磨钢厚度截面组织性能演变规律进行了研究。结果表明,淬火态耐磨钢厚度截面呈表层硬度高、心部硬度低的梯度分布,回火后表层和心部呈现相反的变化趋势,心部/表面硬度比从70%升至93%,1/4处和心部冲击功降低。厚度截面组织和析出相的差异影响固溶强化和析出强化效果,是性能演变的本质原因,提高淬火冷却速度,改善淬火态厚度截面均匀性是提高性能均匀性和优化应用性能的根本方法。 By means of OLYMPUS GX71 optical microscope,field emission scanning electron microscope(FESEM)Quanta450 and JEM2100 F transmission electron microscope(TEM),the evolution of microstructure and properties of thickness section of 60 mm thick wear resistant steel at quenched and quenched+tempered state was studied.The results show that the hardness of quenched wear-resistant steel is gradient distribution with high hardness on the surface and low hardness in the core.After tempering,the hardness ratio of core to surface increases from 70%to 93%,and the impact energy at 1/4 and center of the section decreases.The difference of thickness cross-section microstructure and precipitation phase has great effects on solution strengthen and precipitation strengthen,which is the main reason of performance evolution.Increasing quenching cooling rate and improving the uniformity of quenched thickness section are the fundamental methods to improve uniformity and optimize application performance.
作者 何亚元 李利巍 尹云洋 邓照军 HE Ya-yuan;LI Li-wei;YIN Yun-yang;DENG Zhao-jun(Hot Rolling Products Research Institute of Baosteel Central Research Institute,Wuhan 430080,Hubei,China)
出处 《钢铁研究学报》 CAS CSCD 北大核心 2020年第6期512-518,共7页 Journal of Iron and Steel Research
关键词 耐磨钢 厚度 固溶强化 析出强化 冷却速度 wear-resistant steel thickness solution strengthening precipitation strengthening cooling rate
  • 相关文献

参考文献16

二级参考文献147

共引文献349

同被引文献56

引证文献6

二级引证文献23

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部