Preparation,structure and mechanical properties of Sialon ceramics by transition metal-catalyzed nitriding reaction 被引量:4

原文传递
导出
摘要 Sialon ceramics were prepared by the nitridation of Si,Al and Al2O3 powders with the transition metals(Fe Co,Ni)catalysts.The phase composition,microstructure and mechanical properties of specimens were studied Compared with the catalyst-free specimen,the addition of Fe,Co and Ni greatly promoted the nitridation process of Sialon ceramics and improved the weight gain rate and mechanical properties of specimens.With the increased content of catalysts,the apparent porosity of the products decreased first and then increased,contrary to flexural strength and compressive strength.The specimen with 2.5 wt%Fe had the highest flexural strength 145.8 MPa and it exhibited the highest compressive strength of 594.6 MPa when Co content was 2.5 wt%,whereas they were 71.9 and 78.7 MPa,respectively,when without catalyst.
出处 《Rare Metals》 SCIE EI CAS CSCD 2020年第5期589-596,共8页 稀有金属(英文版)
基金 financially supported by the National Natural Science Foundation of China(Nos.51772140 and 51862024) the Natural Science Foundation of Jiangxi Province(No.20171ACB21033) the Science and Technology Project of the Education Department of Jiangxi Province(No.GJJ170573) the Graduate Innovation Special Fund of Nanchang Hangkong University(No.YC2018-S358)。
  • 相关文献

参考文献7

二级参考文献19

共引文献22

同被引文献22

引证文献4

二级引证文献7

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部