热轧变形量对铝热法制备的2507双相不锈钢组织和力学性能的影响 被引量:2

Effect of hot rolling deformation on microstructure and mechanical properties of 2507 duplex stainless steel prepared via the aluminothermic reaction
下载PDF
导出
摘要 对铝热反应制备的微纳结构2507双相不锈钢在1000℃下进行了变形量为40%、60%和80%的轧制处理.利用X射线衍射仪(XRD)、光学显微镜(OM)、扫描电镜(SEM)、透射电镜(TEM)研究其轧制态显微组织.采用万能拉伸试验机和布洛维光学硬度计测试其力学性能.测试结果表明:轧制过程中,奥氏体和铁素体沿轧制方向被拉长,且奥氏体向铁素体转变.随着轧制变形量的增加,纳米晶平均晶粒尺寸变化不大,但体积分数减小.1000℃下轧制变形量为40%、60%和80%后的屈服强度分别为232、284、456 MPa,抗拉强度分别为533、577、582 MPa,硬度分别为325、330、337 HV,延伸率分别为12.5%、11.1%和11.5%. The 2507 duplex stainless steel with nano/micro-crystalline structure prepared by the aluminothermic reaction was subjected to a rolling treatment at 1000℃with 40%,60%and 80%deformation.The microstructure of the as-rolled state was investigated by X-ray diffraction(XRD),optical microscopy(OM),scanning electron microscopy(SEM),and transmission electron microscopy(TEM).The mechanical properties were measured by using a universal tensile testing machine and a Brook field optical hardness measuring instrument respectively.All measured results show that the rolling process makes austenite and ferrite phases elongated along the rolling direction and the transformation of austenite to ferrite happens in the steel as a result.With increase of rolling deformation,the nanocrystalline size does not change too much,while volume fraction of the nanocrystalline decreases.The yield strength of the steel is about 232,284,456 MPa,tensile strength is about 533,577,582 MPa,hardness is 325,330,337 HV,elongation takes 12.5%,11.1%and 11.5%when the steel was rolled at 1000℃with 40%,60%and 80%deformation,respectively.
作者 喇培清 石玉 汪科良 盛捷 李正宁 周学渊 LA Pei-qing;SHI Yu;WANG Ke-liang;SHENG Jie;LI Zheng-ning;ZHOU Xue-yuan(State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals,Lanzhou Univ.of Tech.,Lanzhou 730050,China)
出处 《兰州理工大学学报》 CAS 北大核心 2020年第4期1-5,共5页 Journal of Lanzhou University of Technology
基金 国家自然科学基金(51561020)。
关键词 2507双相不锈钢 微纳结构 轧制 强度 2507 duplex stainless steel micro/nano-crystalline structure rolling strength
  • 相关文献

参考文献3

二级参考文献27

  • 1罗武庭.DJ—2可变矩形电子束曝光机的DMA驱动程序[J].LSI制造与测试,1989,10(4):20-26. 被引量:373
  • 2Charles J. The duplex stainless steels: materials to meet your needs [ C ]//Duplex stainless steels ' 91 conference. Beaune: Les Editions de Physique,1991:3 -48.
  • 3Bernhardsson. Low alloyed duplex stainless steel : alloy design and properties [ C ]//Duplex stainless steels ' 91 conference. Beaune: Les Editions de Physique, 1991 : 135 - 150.
  • 4Charles J. Super - duplex stainless steels: structure and properties [ C ]//Duplex stainless steels ' 91 conference. Beaune: Les Editions de Physique, 1991 : 151 - 168. Linder M. Report EUR 22082 EN [ R ]. European commission: RFCS publication, 2006.
  • 5Lovland P. Duplex stainless steels 97 [ C ]. Hague : NL Stainless Steel World, 1997.
  • 6Oberi R,Tamba R. Duplex conference 2000 [ C]. Venezia: Duplex conference ,2000.
  • 7Kobayashi M. ISSF 2005 & 2008 Duplex Stainless Steel Survey [ R ]. Brussels : ISSF Publications.
  • 8Hochmanu J. Properties of high chromium ferritic stainless steels and austeno - ferritic stainless steels, in NACE - 5 stress corrosion cracking and hydrogen embrittlement of iron base alloys [ C ]//Proceedings of Unieux - Firminy June 73 conference. Houston: National Association of Corrosion Engineers, 1977:956 - 1002.
  • 9Holtzer J. Brevets francais803 - 361 ( 1953 ), 49. 211 (1937) ,866 -685 (1940) and 803361 ( + PV 40089).
  • 10Liljas M. 80 years with duplex stainless steels, a historic review and prospects for the future [ C ]//NACE Corrosion 94 Conference. Houston: National Association of Corrosion Engineers, 1994.

共引文献39

同被引文献19

引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部